DEVELOPMENT OF AN ELECTROLESS CONIZNP SOLUTION FOR HIGH COERCIVITY FILMS

被引:6
作者
MATSUDA, H
TAKANO, O
机构
[1] Department of Materials Science and Engineering, Himeji Institute of Technology, Hyogo, 671-22, 2167, Shosha, Himeji
关键词
Sodium malonate - Sodium succinate;
D O I
10.1007/BF00625579
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
This paper describes the development of an electrolessly deposited CoNiZnP film for use in magnetic storage devices. A low temperature type solution, which can be operated at 310 K, has been developed. High coercivity films, which have a coercivity of 135 kA m(-1) (1700 Oe) at a film thickness of 80 nm, are deposited from the solution
引用
收藏
页码:1083 / 1088
页数:6
相关论文
共 16 条
[1]  
BRENNER A, 1946, J RES NBS, V37, P1
[2]   PREPARATION AND MAGNETIC CHARACTERISTICS OF CHEMICALLY DEPOSITED COBALT FOR HIGH-DENSITY STORAGE [J].
FISHER, RD ;
CHILTON, WH .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1962, 109 (06) :485-490
[3]   The Structure of Electroless Cobalt Films as Revealed by Electron Microscopy [J].
Jones, G. A. ;
Middleton, B. K. .
JOURNAL OF MATERIALS SCIENCE, 1968, 3 (05) :519-523
[4]  
LATIMER, 1956, OXIDATION STATE ELEM, P43
[5]  
Matsuda H., 1989, Transactions of the Institute of Electronics, Information and Communication Engineers C-II, VJ72C-II, P24
[6]  
MATSUDA H, 1986, 73TH C MET SOC JPN, P98
[7]  
MATSUDA H, 1988, J JPN I MET, V52, P524
[8]  
NISHIDA H, 1991, THESIS HIMEJI I TECH
[9]  
SORAYA M, 1967, PLATING, V54, P549
[10]  
TAKANO O, 1985, MET FINISH, V83, P63