COMPRESSIVE DEFORMATION BEHAVIOR OF LONG RANGE ORDERED POLYCRYSTALLINE IRON-ALUMINUM ALLOYS

被引:78
作者
LEAMY, HJ
KAYSER, FX
机构
[1] Institute for Atomic Research, Department of Metallurgy, Iowa State University, Ames, Iowa
[2] Bell Telephone Laboratories, Murray Hill, New Jersey
来源
PHYSICA STATUS SOLIDI | 1969年 / 34卷 / 02期
关键词
D O I
10.1002/pssb.19690340240
中图分类号
O469 [凝聚态物理学];
学科分类号
070205 ;
摘要
The compressive deformation behavior of polycrystalline iron‐aluminum alloys has been investigated (i) at 298°K for specimens heat treated in various ways and containing from 22.0 to 31.7 at% Al, and (ii) from 77 to 655°K for well‐annealed specimens containing 26.6 at% Al. Alloys which possess significant DO3 type long range order exhibit marked composition and temperature dependent variations in deformation behavior. Specifically, those containing ⪆ 27 at% Al exhibit two linear and one parabolic deformation stage at 298°K. The linear stages are shown to be a result of the production and motion of DO3 type superlattice dislocations. The absence of these stages in well‐annealed specimens is attributed to the lack of thermal assistance for the DO3 superlattice dislocation nucleation process. The flow stress levels which characterize the two linear stage behavior agree with calculations of the stress required for production of antiphase boundaries. Results obtained from quenched specimens are in agreement with the above conclusions, and the changes induced by quenching are in accord with calculations of the effect of thermal antiphase boundaries upon dislocation motion. Copyright © 1969 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim
引用
收藏
页码:765 / &
相关论文
共 46 条
[1]  
BROWN N, 1956, T AM I MIN MET ENG, V206, P1353
[2]   THE YIELD POINT OF A SUPER-LATTICE [J].
BROWN, N .
PHILOSOPHICAL MAGAZINE, 1959, 4 (42) :693-704
[3]   TWINNING IN IRON-ALUMINIUM ALLOYS [J].
CAHN, RW ;
COLL, JA .
ACTA METALLURGICA, 1961, 9 (02) :138-148
[4]  
COTTRELL AH, 1953, RELATION PROPERTIES, P131
[6]  
ELLIOTT RP, 1965, CONSTITUTION BINA S1
[7]   ON THE STRENGTH OF SOLID SOLUTION ALLOYS [J].
FISHER, JC .
ACTA METALLURGICA, 1954, 2 (01) :9-10
[8]  
FLINN PA, 1960, T AM I MIN MET ENG, V218, P145
[9]   CRITICAL SCATTERING OF X-RAYS FROM FE3AL [J].
GUTTMAN, L ;
SCHNYDERS, HC .
PHYSICAL REVIEW LETTERS, 1969, 22 (11) :520-+
[10]  
GUTTMAN L, 1969, PHYS REV LETTERS, V22, P522