EVIDENCE OF CHEMICAL EFFECTS IN NIOBIUM IMPLANTED OXIDES

被引：14

作者：

RAMOS, SMM ^{[1
]}

CANUT, B ^{[1
]}

GEA, L ^{[1
]}

ROMANA, L ^{[1
]}

LEBRUSQ, J ^{[1
]}

THEVENARD, P ^{[1
]}

BRUNEL, M ^{[1
]}

机构：

[1] CNRS, CRISTALLOG LAB, F-38042 GRENOBLE, FRANCE

来源：

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS | 1991年 / 59卷 / pt 2期

关键词：

D O I：

10.1016/0168-583X(91)95793-D

中图分类号：

TH7 [仪器、仪表];

学科分类号：

0804 ; 080401 ; 081102 ;

摘要：

We have investigated the influence of chemical bonding and structure of different oxides on niobium implantation effects. For this purpose, single crystals of alpha-Al2O3, TiO2, MgO and amorphous SiO2 have been implanted with 150 keV Nb+ ions and fluences ranging from 10(16) up to 10(17) ions cm-2. Two different behaviours have been observed depending on ionicity of the studied materials. For more covalent oxides such as alpha-Al2O3, TiO2 and SiO2 implanted with low fluences, the implantation profiles are in good agreement with theoretical predictions (TRIM). For high doses (> 5 X 10(16) ions cm-2) the formation of an amorphous layer has been observed in sapphire and rutile. For a typical ionic oxide such as MgO an anomalous depth distribution profile of implanted particles is observed and the major part of implanted niobium is in substitutional sites. The amorphization is not observed even for the highest implantation doses. These results suggest that different chemical effects occur and they could be correlated with the ability to deform octahedral sites in these oxides and space charge effects.

引用

页码：1201 / 1204

页数：4

共 15 条

[1] LATTICE DISORDER IN ALPHA-AL2O3 INDUCED BY NIOBIUM IMPLANTATION [J].

CANUT, B ;

ROMANA, L ;

THEVENARD, P ;

MONCOFFRE, N .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1990, 46 (1-4) :128-132

[2]

CLINARD F, 1986, RAD EFFECTS NONMETAL, pCH7

[3]

DURAND C, 1985, THESIS U C BERNARD L

[4] ION-BEAM MIXING EFFECTS IN AG PRECIPITATES EMBEDDED IN MGO CRYSTALS [J].

FUCHS, G ;

ABOUCHACRA, G ;

TREILLEUX, M ;

THEVENARD, P ;

SERUGHETTI, J .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1988, 32 (1-4) :100-103

[5] EVIDENCE OF NEW PHASE CREATION IN IMPLANTED TIO2 [J].

GUERMAZI, M ;

THEVENARD, P ;

DUPIN, JP ;

DUPUY, CHS .

NUCLEAR INSTRUMENTS & METHODS, 1981, 182 (APR) :397-406

[6] PHASE-CHANGES IN INSULATORS PRODUCED BY PARTICLE BOMBARDMENT [J].

KELLY, R .

NUCLEAR INSTRUMENTS & METHODS, 1981, 182 (APR) :351-378

[7]

MAZZOLDI P, 1987, ION BEAM MODIFICATIO

[8] THE RESIDUAL CHARGE STATE OF TIN IMPLANTED INTO SAPPHIRE [J].

MCHARGUE, CJ ;

SKLAD, PS ;

MCCALLUM, JC ;

WHITE, CW ;

PEREZ, A ;

ABONNEAU, E ;

MAREST, G .

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1990, 46 (1-4) :74-78

[9]

MCHARGUE CJ, 1990, NUCL INSTRUM METH B, V46, P78

[10]

MCHARGUE CJ, 1985, NUCL INSTRUM METH B, V10, P560

← 1 2 →