EXPERIMENTAL OPTIMIZATION OF ALKALINE ZINC-SILVER OXIDE PRIMARY-CELL WITH RESPECT TO THE ZINC ELECTRODE PREPARATION AND COMPOSITION

被引：8

作者：

POA, SP

LEE, SJ

机构：

[1] Department of Industrial Chemistry, National Tsing Hua University, Hsin-Chu

来源：

JOURNAL OF APPLIED ELECTROCHEMISTRY | 1979年 / 9卷 / 03期

关键词：

D O I：

10.1007/BF01112484

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The optimization of parameters controlling the fabrication of zinc electrodes, by the slurry paste method, has been carried out. The parameters varied were active material composition, applied compression and electrode thickness. The optimum values obtained by a factorial experimental programme were: a zinc material that contains 2-4 wt% HgO, 0·5-2% PVA, and 94-97·5% ZnO; a compression of 500-1500 psi applied to the zinc electrode; and an electrode thickness of 0·265-0·35 mm. © 1979 Chapman and Hall Ltd.

引用

收藏

页码：307 / 313

页数：7

相关论文

共 25 条

[1] CONTROLLED CURRENT DEPOSITION OF ZINC FROM ALKALINE SOLUTION [J].

AROUETE, S ;

BLURTON, KF ;

OSWIN, HG .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1969, 116 (02) :166-&

[2] DEPOSITION AND DISSOLUTION OF ZINC IN ALKALINE SOLUTIONS [J].

BOCKRIS, JOM ;

NAGY, Z ;

DAMJANOVIC, A .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1972, 119 (03) :285-+

[3] DISSOLUTION AND PASSIVATION OF VERTICAL POROUS ZINC ELECTRODES IN ALKALINE SOLUTION [J].

BREITER, MW .

ELECTROCHIMICA ACTA, 1970, 15 (08) :1297-&

[4] ANODIC BEHAVIOR OF POROUS ZINC ELECTRODES .2. EFFECTS OF SPECIFIC SURFACE-AREA OF ZINC COMPACT MATERIAL [J].

COATES, G ;

HAMPSON, NA ;

MARSHALL, A ;

PORTER, DF .

JOURNAL OF APPLIED ELECTROCHEMISTRY, 1974, 4 (01) :75-80

[5]

DEHAHAY P, 1965, DOUBLE LAYER ELECTRO

[6] KINETICS AND MECHANISM OF DEPOSITION OF ZINC FROM ZINCATE IN CONCENTRATED ALKALI HYDROXIDE SOLUTIONS [J].

DESPIC, AR ;

JOVANOVIC, D ;

RAKIC, T .

ELECTROCHIMICA ACTA, 1976, 21 (01) :63-77

[7]

DESPIC AR, 1974, J ELECTROCHEM SOC, V121, P121

[8] INHIBITION OF DENDRITIC ELECTROCRYSTALLIZATION OF ZINC FROM DOPED ALKALINE ZINCATE SOLUTIONS [J].

DIGGLE, JW ;

DAMJANOVIC, A .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1972, 119 (12) :1649-+

[9] MECHANISM OF DENDRITIC ELECTROCRYSTALLIZATION OF ZINC [J].

DIGGLE, JW ;

DESPIC, AR ;

BOCKRIS, JO .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1969, 116 (11) :1503-&

[10] ZN(II)/ZN EXCHANGE-REACTION IN KOH SOLUTION .1. EXCHANGE CURRENT-DENSITY MEASUREMENTS USING GALVANOSTATIC METHOD [J].

DIRKSE, TP ;

HAMPSON, NA .

ELECTROCHIMICA ACTA, 1972, 17 (01) :135-&