INFLUENCE OF OXYGEN ON VOID FORMATION IN NEUTRON-IRRADIATED VANADIUM

被引：7

作者：

BRESSERS, J ^{[1
]}

VANWITZENBURG, W ^{[1
]}

机构：

[1] NETHERLANDS ENERGY RES FDN,ECN,PETTEN,NETHERLANDS

来源：

JOURNAL OF NUCLEAR MATERIALS | 1979年 / 85-6卷 / DEC期

关键词：

D O I：

10.1016/0022-3115(79)90352-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The influence of oxygen on void formation in mono- and poly-crystalline vanadium, neutron irradiated to fluences up to 2.5 × 1025n/m2 (E > 1 MeV) in the temperature range 673-1073 K, was experimentally investigated. The oxygen doped samples contained 850 appm oxygen initially, while the initial oxygen content of the pure samples was less than 40 appm. The oxygendoped materials in general show larger void concentrations but smaller voids, particularly in the mono-crystalline material, while the effect of oxygen on the void volume fraction is very small. Even at very high void concentrations, no indication of void lattice formation has been observed. © 1979.

引用

页码：757 / 761

页数：5

共 20 条

[1]

AGARWAL SC, 1977, T AM NUCL SOC, V26, P184

[2]

AGARWAL SC, 1975, INT C RAD EFFECTS TR

[3]

AGARWAL SC, 1976, ASTMSTP611, P298

[4]

BARTLETT AF, 1975, INT C RAD EFFECTS TR

[5]

BENTLEY J, 1975, INT C FUNDAMENTAL AS, P925

[6] PREPARATION AND CHARACTERIZATION OF HIGH-PURITY VANADIUM BY EBFZM [J].

BRESSERS, J ;

CRETEN, R ;

VANHOLSBEKE, G .

JOURNAL OF THE LESS-COMMON METALS, 1975, 39 (01) :7-16

[7]

Brimhall J. L., 1970, Radiation Effects, V3, P203, DOI 10.1080/00337577008236275

[8]

CARLANDER R, 1973, ASTMSTP529, P399

[9] VOIDS IN VANADIUM, NIOBIUM AND MOLYBDENUM BY FAST NEUTRON IRRADIATION AT HIGH TEMPERATURES [J].

ELEN, JD ;

HAMBURG, G ;

MASTENBROEK, A .

JOURNAL OF NUCLEAR MATERIALS, 1971, 39 (02) :194-+

[10]

ELEN JD, 1970, MICROSCOPIE ELECTRON, V2, P351

← 1 2 →