INFLUENCE OF WATER SORPTION ON ACRYLIC POLYMER WAVE-GUIDE LOSS

被引：4

作者：

HIDA, Y

IMAMURA, S

机构：

[1] NTT Opto-electronics Laboratories, Naka-Gun, Ibaraki-ken, 319-11, 162, Tokai-mura

来源：

IEEE PHOTONICS TECHNOLOGY LETTERS | 1994年 / 6卷 / 07期

关键词：

D O I：

10.1109/68.311474

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

The influence Of Water sorption on acrylic polymer waveguides was studied by measuring the loss changes in the atmosphere at 13 to 98 %RH. The absorption peak at 1.41 mum increased from 0.5 to 2 Db/cm due to water sorption. This peak resulted in a small loss change of 0.03 dB/cm at 1.3 mum, which was successfully measured using a 57 cm waveguide with a loss of around 0.1 dB/cm. Relationships between loss change and water sorption were also revealed by measuring the water content of the polymers.

引用

页码：845 / 847

页数：3

共 7 条

[1] LOW-LOSS CHANNEL WAVE-GUIDES IN POLYMERS
BOOTH, BL
[J]. JOURNAL OF LIGHTWAVE TECHNOLOGY, 1989, 7 (10) : 1445 - 1453
[2] RING RESONATOR COMPOSED OF LOW-LOSS POLYMER WAVE-GUIDES AT 1.3-MU-M
HIDA, Y
IMAMURA, S
IZAWA, T
[J]. ELECTRONICS LETTERS, 1992, 28 (14) : 1314 - 1316
[3] POLYMER WAVE-GUIDE THERMOOPTIC SWITCH WITH LOW ELECTRIC-POWER CONSUMPTION AT 1.3 MU
HIDA, Y
ONOSE, H
IMAMURA, S
[J]. IEEE PHOTONICS TECHNOLOGY LETTERS, 1993, 5 (07) : 782 - 784
[4] POLYMER CHANNEL WAVE-GUIDES WITH LOW-LOSS AT 1.3 MU-M
IMAMURA, S
YOSHIMURA, R
IZAWA, T
[J]. ELECTRONICS LETTERS, 1991, 27 (15) : 1342 - 1343
[5] IZAWA T, 1991, ECOCIOOC 91 PARIS
[6] INFLUENCE OF WATER-ABSORPTION ON PLASTIC OPTICAL FIBERS
KAINO, T
[J]. APPLIED OPTICS, 1985, 24 (23) : 4192 - 4195
[7] THOMAS AM, 1951, J APPL CHEM, V1, P141

← 1 →