DIFFERENTIAL THERMAL-ANALYSIS OF HYDROGEN-INDUCED AMORPHIZATION IN C15 LAVES PHASE GDFE2

被引:33
作者
AOKI, K
LI, XG
MASUMOTO, T
机构
[1] Institute for Materials Research, Tohoku University, Sendai
来源
ACTA METALLURGICA ET MATERIALIA | 1992年 / 40卷 / 02期
关键词
D O I
10.1016/0956-7151(92)90297-R
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Stuctural changes of the C15 Laves phase GdFe2 during differential thermal analysis in a hydrogen atmosphere have been investigated by X-ray diffraction and transmission electron microscopy. The DTA curves exhibit four exothermic peaks resulting from hydrogen absorption, hydrogen-induced amorphization (HIA), precipitation of GdH2 and crystallization. As the hydrogen pressure increases, the onset temperatures of hydrogen absorption, HIA and crystallization become lower. Correspondingly, the activation energies for hydrogen absorption and for HIA decrease from 125 to 110 kJ/mol and from 130 to 95 kJ/mol, respectively, but that for the precipitation of GdH2 is almost constant as 200 kJ/mol. These results indicate that as the hydrogen pressure increases, both the hydrogen absorption and amorphization occur easily.
引用
收藏
页码:221 / 227
页数:7
相关论文
共 12 条
  • [1] AMORPHIZATION OF RFE2 LAVES PHASES BY HYDROGEN ABSORPTION
    AOKI, K
    YANAGITANI, A
    LI, XG
    MASUMOTO, T
    [J]. MATERIALS SCIENCE AND ENGINEERING, 1988, 97 : 35 - 38
  • [2] AOKI K, 1988, SCI REP RES TOHOKU A, V34, P79
  • [3] CRYSTALLINE TO AMORPHOUS TRANSFORMATION IN LAVES PHASE GDFE2 INDUCED BY HYDROGEN ABSORPTION
    AOKI, K
    YANAGITANI, A
    MASUMOTO, T
    [J]. APPLIED PHYSICS LETTERS, 1988, 52 (25) : 2122 - 2123
  • [4] HYDROGEN-INDUCED AMORPHIZATION AND ITS EFFECT ON MAGNETIC-PROPERTIES OF THE LAVES-PHASE GDFE2 COMPOUND
    AOKI, K
    NAGANO, M
    YANAGITANI, A
    MASUMOTO, T
    [J]. JOURNAL OF APPLIED PHYSICS, 1987, 62 (08) : 3314 - 3317
  • [5] DIFFERENTIAL THERMAL-ANALYSIS OF HYDROGEN-INDUCED AMORPHIZATION IN C15 LAVES COMPOUNDS GDFE2, GDCO2, GDNI2 (M=FE, CO, NI)
    AOKI, K
    LI, XG
    MASUMOTO, T
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 133 : 565 - 568
  • [6] HYDROGEN SITE OCCUPANCY IN AB2 LAVES PHASES
    IVEY, D
    NORTHWOOD, D
    [J]. JOURNAL OF THE LESS-COMMON METALS, 1986, 115 (01): : 23 - 33
  • [7] THERMODYNAMIC AND KINETIC ASPECTS OF THE CRYSTAL TO GLASS TRANSFORMATION IN METALLIC MATERIALS
    JOHNSON, WL
    [J]. PROGRESS IN MATERIALS SCIENCE, 1986, 30 (02) : 81 - 134
  • [8] KISSINGER HE, 1957, ANAL CHEM, V291, P705
  • [9] CHANGES IN SHORT-RANGE ORDER RESULTING FROM HYDROGEN ABSORPTION OF FE2CE AND FE2ER METALLIC GLASSES
    MATSUURA, M
    FUKAMICHI, K
    KOMATSU, H
    AOKI, K
    MASUMOTO, T
    SUZUKI, K
    [J]. MATERIALS SCIENCE AND ENGINEERING, 1988, 97 : 223 - 226
  • [10] SAXCE TD, 1985, J LESS-COMMON MET, V107, P35