A DAMAGE MECHANICS MODEL OF FATIGUE CRACK INITIATION IN NOTCHED PLATES

被引：33

作者：

CHOW, CL ^{[1
]}

WEI, Y ^{[1
]}

机构：

[1] UNIV HONG KONG,DEPT MECH ENGN,HONG KONG,HONG KONG

来源：

THEORETICAL AND APPLIED FRACTURE MECHANICS | 1991年 / 16卷 / 02期

关键词：

D O I：

10.1016/0167-8442(91)90029-J

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

A damage model is proposed to characterize fatigue crack initiation in notched plates. This is accomplished by assuming a damage fracture criterion and effective instantaneous tangent moduli matrix which accounts for damage accumulation. A finite element package is used to perform the numerical analyses for an edge-notched plate specimen made of Al alloy 2024-T3 under cyclic loading of varying constant amplitudes. The estimated fatigue crack initiation life agrees satisfactorily with those determined experimentally. An important observation from the results of the proposed damage model is its ability to identify the phenomenon of stress redistribution due to material degradation in two-dimension specimens during fatigue loading.

引用

页码：123 / 133

页数：11

共 10 条

[1]

BEAUMONT PWR, 1987, DAMAGE MECHANICS AD, V12

[2]

CHABOCHE JL, 1987, RECH AEROSPATIALE, P38

[3]

CHOW CL, 1988, INT J FRACTURE, V38, P83

[4]

CHOW CL, IN PRESS INT J FRACT

[5]

Frost N.E., 1974, OXFORD ENG SCI SERIE, P130

[6]

Kachanov LM, 1958, IZVESTIIA AKAD NAUK, V8, P26, DOI DOI 10.1023/A:1018671022008

[7] LOCAL APPROACH OF FRACTURE [J].

LEMAITRE, J .

ENGINEERING FRACTURE MECHANICS, 1986, 25 (5-6) :523-537

[8] DAMAGE MEASUREMENTS [J].

LEMAITRE, J ;

DUFAILLY, J .

ENGINEERING FRACTURE MECHANICS, 1987, 28 (5-6) :643-&

[9]

LU TJ, IN PRESS HYPOTHESIS

[10]

[No title captured]

← 1 →