EFFECTS OF MORPHOLOGY ON NO2 DETECTION IN AIR AT ROOM-TEMPERATURE WITH PHTHALOCYANINE THIN-FILMS

被引:71
作者
SADAOKA, Y
JONES, TA
REVELL, GS
GOPEL, W
机构
[1] UNIV TUBINGEN,INST PHYS & THEORET CHEM,W-7400 TUBINGEN 1,GERMANY
[2] HLTH & SAFETY EXECUT,DIV RES & LAB SERV,SHEFFIELD S3 7HQ,ENGLAND
关键词
D O I
10.1007/BF00580159
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Lead phthalocyanine films freshly deposited on alumina and glass were found to consist of disordered phases and fine particles with mean diameter below 0.2μm. Following annealing at 300 ° C, a transition to a crystalline form is obtained. The crystal size in the films annealed at 300 ° C or above is affected by the nature of the substrate, ambient atmosphere and annealing time. Following an optimized preparation procedure, the films exhibit response times of less than 20 sec and recovery times of the order of several minutes, independently of N02 concentration or exposure time, at room temperature. They consist of fine crystals with mean diameters of the order of 0.2μm and amorphous phases are not observed. For zinc, copper, cobalt and nickel phthalocyanine films, some improvements in the response and recovery times are achieved by annealing but not sufficient to allow No2 detection at room temperature. For films of these phthalocyanines, fine crystals of the type formed in leadphthalocyanine films were not produced in the conductive paths when the films were annealed at 300 ° C in air. © 1990 Chapman and Hall Ltd.
引用
收藏
页码:5257 / 5268
页数:12
相关论文
共 14 条
[1]   A HIGHLY SENSITIVE NO2 SENSOR BASED ON ELECTRICAL-CONDUCTIVITY CHANGES IN PHTHALOCYANINE FILMS [J].
BOTT, B ;
JONES, TA .
SENSORS AND ACTUATORS, 1984, 5 (01) :43-53
[2]   PHASE-BEHAVIOR OF COBALT, NICKEL AND ZINC PHTHALOCYANINES [J].
COLLINS, RA ;
MOHAMMED, KA .
THERMOCHIMICA ACTA, 1987, 109 (02) :397-402
[3]   INFRARED SPECTRA OF ORGANIC COMPOUNDS EXHIBITING POLYMORPHISM [J].
EBERT, AA ;
GOTTLIEB, HB .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1952, 74 (11) :2806-2810
[4]  
GUTMANN F, 1967, ORGANIC SEMICONDUCTO, P197
[5]  
HONEYBOURNE CL, 1984, J PHYS CHEM SOLIDS, V44, P43
[6]   LEAD PHTHALOCYANINE (PBPC) AS A PROTOTYPE ORGANIC MATERIAL FOR GAS SENSORS - COMPARATIVE ELECTRICAL AND SPECTROSCOPIC STUDIES TO OPTIMIZE O-2 AND NO2 SENSING [J].
MOCKERT, H ;
SCHMEISSER, D ;
GOPEL, W .
SENSORS AND ACTUATORS, 1989, 19 (02) :159-176
[7]  
RAGER A, 1989, J MOL ELECTRON, V5, P227
[8]  
SADAOKA Y, 1978, DENKI KAGAKU, V46, P597
[9]  
SADAOKA Y, 1980, DENKI KAGAKU, V48, P486
[10]   EFFECT OF HEAT PRETREATMENT ON THE ELECTRICAL CONDUCTANCE OF LEAD PHTHALOCYANINE FILMS FOR NO2 GAS-DETECTION [J].
SADAOKA, Y ;
JONES, TA ;
GOPEL, W .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1989, 8 (09) :1095-1097