A FATIGUE-CRACK-GROWTH-BASED ANALYSIS OF 2-STEP CORROSION-FATIGUE TESTS

被引：12

作者：

ISHIHARA, S

MCEVILY, AJ

SHIOZAWA, K

机构：

[1] UNIV CONNECTICUT,DEPT MET,STORRS,CT

[2] UNIV CONNECTICUT,INST MAT SCI,STORRS,CT

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 1995年 / 18卷 / 11期

关键词：

D O I：

10.1111/j.1460-2695.1995.tb00857.x

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

A method for the analysis of two-step fatigue level sequences is proposed and compared with experimental results. Two-step loading tests of the aluminum alloy 2017-T4 in 3% sodium chloride solution have been carried out in conjunction with a replica technique used to monitor the growth of fatigue cracks. Fatigue cracks were nucleated at corrosion pits 10-15 mu m in size, and crack growth rather than crack initiation was found to take up the major portion of the fatigue lifetime in these tests. The results could therefore be analyzed on the basis of the following constitutive relation for fatigue crack growth: da/dN = A(Delta K-eff - Delta K-effth)(2) This analysis was simplified since the influence of transients in the crack growth rate induced upon change in load level was found to be minimal. The approach provides a rational basis for dealing with load-sequence effects.

引用

页码：1311 / 1321

页数：11

共 29 条

[1]

Barsom JM., 1976, FATIGUE CRACK GROWTH, V595, P217, DOI [10.1520/STP33374S, DOI 10.1520/STP33374S]

[2]

Corten H.T., 1956, P INT C FATIGUE META, V1, P235

[3]

GATTS RR, 1961, T ASME, V83, P529

[4]

GOTO M, 1989, JAPAN SOC MECH ENG, V55, P453

[5]

GROVER HJ, 1960, ASTM STP, V274, P120

[6]

HARDRATH HF, 1964, FATIGUE INTERDISCIPL, P345

[7] CUMULATIVE DAMAGE THEORY OF FATIGUE FAILURE [J].

HASHIN, Z ;

ROTEM, A .

MATERIALS SCIENCE AND ENGINEERING, 1978, 34 (02) :147-160

[8]

HASHIN Z, 1980, FATIGUE ENG MATER ST, V2, P345

[9]

Ibrahim MFE, 1980, FATIGUE ENG MATER ST, V2, P351, DOI DOI 10.1111/J.1460-2695.1979.TB01093.X

[10]

Ishihara S., 1984, Journal of the Society of Materials Science, Japan, V33, P901, DOI 10.2472/jsms.33.901

← 1 2 3 →