ON MECHANISM OF INTERSTITIAL-IMPURITY-INDUCED CROSS-SLIP IN IRON DEFORMED NEAR 175 DEGREES K

被引:20
作者
CHRIST, BW
机构
[1] Metallurgy Division, Institute for Materials Research, National Bureau of Standards, Washington
来源
ACTA METALLURGICA | 1969年 / 17卷 / 10期
关键词
D O I
10.1016/0001-6160(69)90148-5
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
A mechanism is proposed whereby the elastic dipole distortion of stationary interstitial impurity atoms in lattice solution promotes nucleation and stabilization of double-kink-size screw dislocation segments on cross-slip planes. Stress relaxation accompanying interstitial-impurity-induced cross-slip can account for the experimental observations that small atom fractions of nitrogen in lattice solution in iron deformed at temperatures near 175°K decrease yield and flow stresses and increase ductility. © 1969.
引用
收藏
页码:1317 / &
相关论文
共 22 条
  • [1] CHRIST BW, 1968, MEM ETUD SCI REV MET, V65, P207
  • [2] CHRIST BW, IN PRESS
  • [3] CHRIST BW, 1965, THESIS CORNELL U
  • [4] INTERACTION BETWEEN DISLOCATIONS AND INTERSTITIAL ATOMS IN BODY-CENTERED CUBIC METALS
    COCHARDT, AW
    SCHOEK, G
    WIEDERSICH, H
    [J]. ACTA METALLURGICA, 1955, 3 (06): : 533 - 537
  • [5] COHEN M, 1962, T METALL SOC AIME, V224, P638
  • [6] Fleischer R.L., 1964, STRENGTHENING METALS, P93
  • [7] Fleischer R.L., 1963, RELATION STRUCTURE M, P262
  • [8] FRIEDEL J, 1964, DISLOCATIONS, P356
  • [9] ATOMIC DISPLACEMENTS IN IRON MARTENSITE
    KEATING, DT
    GOLAND, AN
    [J]. ACTA METALLURGICA, 1967, 15 (12): : 1805 - &
  • [10] KEH AS, 1963, ELECT MICROSCOPY STR, P231