THERMODYNAMICS OF INCLUSION FORMATION IN FE-TI-C-N ALLOYS

The thermodynamics of the formation of titanium carbonitride in liquid iron-titanium-carbon-nitrogen alloys were investigated in order to predict under what conditions it will form in liquid steel. A metal-carbonitride equilibration technique was used. Titanium carbonitride of a desired composition was made by mixing and high-temperature sintering of very fine powders of titanium nitride and carbide. The formation of titanium carbonitride was confirmed by lattice parameter measurements on the samples before and after the experiments. The equilibrium concentrations of titanium, carbon, and nitrogen in equilibrium with a specific titanium carbonitride were obtained at 1873 K. Activities of titanium carbide and nitride relative to pure solid titanium carbide and nitride were calculated. It was found that titanium carbonitride solid solution is almost ideal. From the results, calculations were performed to predict at which composition various carbonitrides will form. © 1990 The Minerals, Metals & Material Society.