HARDNESS OF IRRADIATED AND HELIUM IMPLANTED DIN-1.4914 MARTENSITIC STAINLESS-STEEL

被引：6

作者：

CHEN, JC

JUNG, P

机构：

[1] Association Euratom -KFA, Institut für Festkörperforschung, Forschungszentrum Jülich

来源：

JOURNAL OF NUCLEAR MATERIALS | 1994年 / 212卷 / pt A期

关键词：

D O I：

10.1016/0022-3115(94)90122-8

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Microhardness of DIN 1.4914 (MANET) martensitic stainless steel, irradiated and helium implanted at room temperature, was measured at temperatures from -180 degrees C to +160 degrees C. Measurements were also performed after annealing at 450 and 650 degrees C and on specimens which were implanted at 600 degrees C and irradiated at 520 degrees C. The results are discussed in terms of the effect of transmutant helium and displacement damage on the ductile to brittle transition temperature.