FABRICATION, STRUCTURE AND PROPERTIES OF MOSI2-BASE COMPOSITES

被引:58
作者
ALMAN, DE
SHAW, KG
STOLOFF, NS
RAJAN, K
机构
[1] Materials Engineering Department, Rensselaer Polytechnic Institute, Troy
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1992年 / 155卷 / 1-2期
关键词
D O I
10.1016/0921-5093(92)90315-R
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Several techniques have been employed to consolidate MoSi2 composites reinforced with either Al2O3 or niobium. Powder injection molding was used to prepare MoSi2 with aligned short FP Al2O3 fibers. Plasma spray was used to produce lamellar MoSi2-Al2O3. Niobium particles, random short fibers and continuous fibers were incorporated into MoSi2 by hot isostatic pressing. Microstructures and mechanical properties of the various composites are reported. Significant microscopic toughening was obtained with continuous niobium fibers, but at the expense of creep resistance.
引用
收藏
页码:85 / 93
页数:9
相关论文
共 10 条
[1]  
ALMAN DE, 1991, LOW DENSITY HIGH TEM, P109
[2]  
CONWAY JB, 1969, R69NSP9 GEN EL CO RE
[3]  
Fitzer E, 1971, HIGH TEMPERATURE HIG, V3, P445
[4]  
GOKHALE AB, 1986, BINARY ALLOY PHASE D
[5]  
HYNES AP, 1991, P AM SOC COMPOSITES, P591
[6]   TOUGHENING OF MOSI2 WITH A DUCTILE (NIOBIUM) REINFORCEMENT [J].
LU, TC ;
EVANS, AG ;
HECHT, RJ ;
MEHRABIAN, R .
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (08) :1853-1862
[7]   SILICIDE-MATRIX MATERIALS FOR HIGH-TEMPERATURE APPLICATIONS [J].
MESCHTER, PJ ;
SCHWARTZ, DS .
JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY, 1989, 41 (11) :52-55
[8]  
SADANANDA K, IN PRESS CREEP MONOL
[9]  
SHAW K, UNPUB
[10]  
[No title captured]