CHELATE MEMBRANE FROM POLY(VINYL ALCOHOL)/POLY(N-SALICYLIDENE ALLYL AMINE) BLEND .2. EFFECT OF CO(II) CONTENT ON OXYGEN NITROGEN SEPARATION

被引:9
作者
CHOI, MJ [1 ]
PARK, CK [1 ]
LEE, YM [1 ]
机构
[1] HANYANG UNIV,COLL ENGN,DEPT IND CHEM,SEOUL 133791,SOUTH KOREA
关键词
D O I
10.1002/app.1995.070581304
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Facilitated transport of oxygen was performed through chelate membranes containing cobalt with selective oxygen binding ability as a fixed oxygen carrier. Chelate membranes were obtained from Schiff base membranes after treating a poly(allyl amine) (PAAm) and poly(vinyl alcohol) (PVA) blend with salicylaldehyde. It is confirmed that the O-O stretching peak through a frequency change in FTIR could be seen at 1150 cm(-1) between cobalt in the membrane and incoming oxygen. The permeability of oxygen through Schiff base membranes was 2.01-2.98 X 10(-13) [cm(3) (STP) cm(2)/cm a cmHg] and oxygen permselectivity was in the range of 1.83-3.27. For chelate membranes, both the permeability of oxygen and oxygen selectivity increased to 2.15-2.82 X 10(-12) [cm(3) (STP) cm(2)/cm s cmHg] and around 8, respectively. Permselectivity of chelate increased as a result of facilitation of O-2 and inhibition of N-2 transport. Detailed results and the mechanism of facilitation of oxygen are discussed on the basis of molecular interactions. (C) 1995 John Wiley & Sons, Inc.
引用
收藏
页码:2373 / 2379
页数:7
相关论文
共 27 条
  • [1] MOLECULAR-TRANSPORT OF OXYGEN AND NITROGEN THROUGH POLYMER-FILMS
    AMINABHAVI, TM
    AITHAL, US
    [J]. JOURNAL OF MACROMOLECULAR SCIENCE-REVIEWS IN MACROMOLECULAR CHEMISTRY AND PHYSICS, 1991, C31 (2-3): : 117 - 163
  • [2] GAS SEPARATION MEMBRANES - A NOVEL APPLICATION FOR CONDUCTING POLYMERS
    ANDERSON, MR
    MATTES, BR
    REISS, H
    KANER, RB
    [J]. SYNTHETIC METALS, 1991, 41 (03) : 1151 - 1154
  • [3] BOHLEN H, 1980, MAKROMOL CHEM-RAPID, V1, P753
  • [4] OXYGEN NITROGEN TRANSPORT IN GLASSY-POLYMERS WITH OXYGEN-BINDING PENDENT GROUPS
    DELANEY, MS
    REDDY, D
    WESSLING, RA
    [J]. JOURNAL OF MEMBRANE SCIENCE, 1990, 49 (01) : 15 - 36
  • [5] HSIUE GH, 1991, MACROMOLECULES, V24, P4010
  • [6] HSIUE GH, 1994, J MEMB SCI, V87, P233
  • [7] HSIUE GH, 1993, J POLYM SCI POL CHEM, V31, P457
  • [8] Inagaki N, 1988, J APPL POLYM SCI APP, V42, P327
  • [9] LIQUID MEMBRANES FOR THE PRODUCTION OF OXYGEN-ENRICHED AIR .2. FACILITATED-TRANSPORT MEMBRANES
    JOHNSON, BM
    BAKER, RW
    MATSON, SL
    SMITH, KL
    ROMAN, IC
    TUTTLE, ME
    LONSDALE, HK
    [J]. JOURNAL OF MEMBRANE SCIENCE, 1987, 31 (01) : 31 - 67
  • [10] Kramer P.W., 1993, US Pat., Patent No. 5215554