THE EFFECT OF HUMIDITY ON THE DURABILITY OF ALUMINUM-EPOXIDE JOINTS

被引：63

作者：

BREWIS, DM

COMYN, J

RAVAL, AK

KINLOCH, AJ

机构：

[1] Department of Chemistry, Leicester Polytechnic, Leicester

[2] Department of Mechanical Engineering, Imperial College, London

来源：

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES | 1990年 / 10卷 / 04期

关键词：

absorption isotherm; critical relative humidity; diffusion; durability; epoxide adhesive; humidity; lap joints;

D O I：

10.1016/0143-7496(90)90042-V

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Single lap joints of sandblasted aluminium alloy have been prepared with anepoxide adhesive based on dgeba and 1, 3-diaminobenzene. They have been exposed to air at 50°C and to a range of humidities for up to 10080 h, and then tested. After 10080 h ageing the results give some evidence for a critical relative humidity at 65%, such that joints weaken to a greater extent if this value is exceeded. Measurement of mass uptake of films of the adhesive suspended in air at various humidities has provided the water absorption isotherm and diffusion coefficients. The isotherm is gently curved and of BET type IV; there are no sharp changes that might account for a critical relative humidity. The presence of salt hydrates at the interface is a feasible explanation for this. © 1990.

引用

页码：247 / 253

页数：7

共 20 条

[1]

Comyn, Durability of Structural Adhesives, (1983)

[2]

DeLollis, Nat SAMPE Symp Exhib, 22, (1977)

[3]

Gledhill, Kinloch, Shaw, J Adhesion, 11, (1980)

[4]

Brewis, Comyn, Cope, Moloney, Polymer, 21, (1980)

[5]

Brewis, Comyn, Cope, Moloney, Polymer, 21, (1980)

[6]

Brewis, Comyn, Cope, Moloney, Polymer Eng Sci, 21, (1981)

[7]

Brewis, Comyn, Tegg, Int J Adhesion Adhesives, 1, (1980)

[8]

Dannenberg, May, Treatise on Adhesion and Adhesives, 2, (1972)

[9]

Brewis, Comyn, Tegg, Polymer, 21, (1980)

[10]

Brewis, Comyn, Shalash, Tegg, Polymer, 21, (1980)

← 1 2 →