CURRENT UNDERSTANDING OF STRESS-CORROSION CRACKING

被引：23

作者：

PARKINS, RN ^{[1
]}

机构：

[1] UNIV NEWCASTLE UPON TYNE,NEWCASTLE TYNE NE1 7RU,TYNE & WEAR,ENGLAND

来源：

JOM-JOURNAL OF THE MINERALS METALS & MATERIALS SOCIETY | 1992年 / 44卷 / 12期

关键词：

D O I：

10.1007/BF03223188

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

For some 100 years, the problem of environment-induced brittle failure of normally ductile alloys has intrigued and perplexed researchers. A variety of mechanisms have been invoked, and while many of them seem to be operative in some instances, they do not all universally apply. This exhaustive review examines the current knowledge of the many mechanisms for stress-corrosion cracking and describes the conditions in which they apply.

引用

页码：12 / 19

页数：8

共 69 条

[1]

ABE S, 1992, PARKINS SYMPOSIUM ON FUNDAMENTAL ASPECTS OF STRESS CORROSION CRACKING, P389

[2]

BAER DR, 1992, PARKINS SYMPOSIUM ON FUNDAMENTAL ASPECTS OF STRESS CORROSION CRACKING, P511

[3]

BALASUBRAMANIAM R, 1992, PARKINS SYMPOSIUM ON FUNDAMENTAL ASPECTS OF STRESS CORROSION CRACKING, P131

[4]

BIRNBAUM HK, 1991, 1991 TMS FALL M CINC

[5]

BIRNBAUM HK, 1990, ENV INDUCED CRACKING, P21

[6]

BUCHHEIT RG, 1992, PARKINS SYMPOSIUM ON FUNDAMENTAL ASPECTS OF STRESS CORROSION CRACKING, P141

[7]

BUONANNO MA, 1992, PARKINS SYMPOSIUM ON FUNDAMENTAL ASPECTS OF STRESS CORROSION CRACKING, P103

[8] EFFECTS OF SEGREGATED PHOSPHORUS ON STRESS-CORROSION CRACKING SUSCEPTIBILITY OF 3CR-0.5MO STEEL [J].

BURSTEIN, GT ;

WOODWARD, J .

METAL SCIENCE, 1983, 17 (03) :111-116

[9]

BUSH SH, 1991, 1991 TMS FALL M CINC

[10]

CHEN CH, 1987, J ELECTROCHEM SOC, V134, P1635

← 1 2 3 4 5 6 7 →