EFFECT OF DIFFERENT ADMIXTURES ON THE DURABILITY OF SULFUR CONCRETE MADE WITH DIFFERENT AGGREGATES

被引：8

作者：

CZARNECKI, B

GILLOTT, JE

机构：

[1] Department of Civil Engineering, The University of Calgary, Calgary, Alta. T2N 1N4

来源：

ENGINEERING GEOLOGY | 1990年 / 28卷 / 1-2期

关键词：

D O I：

10.1016/0013-7952(90)90036-Z

中图分类号：

P5 [地质学];

学科分类号：

0709 [地质学]; 081803 [地质工程];

摘要：

Sulphur concrete made with syenite, granite, diorite, basalt and graywacke aggregate and 20% sulphur binder was found to expand excessively during continuous immersion in water. When the amount of sulphur was increased to 23% moisture expansion decreased but remained unacceptable for concrete made with syenite, granite and basalt aggregate. Concrete made with marble aggregate showed little change in dimensions upon immersion in water. The resonant frequency test showed that the concrete with the largest drop in relative dynamic modulus had the largest moisture expansion and water uptake but the strength retention was high and no cracks were observed on the surface of the specimens. Concrete which contained glycerine and silane admixtures showed reduced moisture expansion. The study showed that weathered rocks and particularly those with a larger specific surface area may cause moisture durability problems if used as aggregate in sulphur concrete; expansion may be greatly reduced by use of proper admixtures. © 1990.

引用

页码：105 / 118

页数：14

共 12 条

[1]

American Society for Testing and Materials, C215, Test Method for Fundamental, Transverse, Longitudinal and Torsional Frequencies of Concrete Specimens, pp. 147-151, (1983)

[2]

Arkles, Tailoring surfaces with silanes, Chem. Technol., 165, pp. 766-778, (1977)

[3]

Brunauer, Emmett, Teller, Adsorption of gases in multimolecular layers, J. Am. Chem. Soc., 60, pp. 309-319, (1938)

[4]

Canadian Standards Association, Test Method for Alkali-Reactivity Using Concrete Prisms, (1977)

[5]

Czarnecki, Durability of Sulphur Concrete, M.Sc. Thesis, (1987)

[6]

Feldman, Beaudoin, Some factors affecting durability of sulphur-impregnated porous bodies, Cement Concrete Res., 8, 3, pp. 273-282, (1978)

[7]

Gillott, Jordaan, Loov, Shrive, Durability studies of sulphur concrete, Durability of Building Materials, and Components, 11, pp. 549-559, (1980)

[8]

Gillott, Jordaan, Loov, Shrive, Sulphur Concretes, Mortars and the Like, (1980)

[9]

Gillott, Jordaan, Loov, Shrive, Effect of different aggregates on durability of sulphur concretes, Durability of Building Materials, 1, pp. 255-273, (1983)

[10]

Gillott, Jordaan, Loov, Raymont, Shrive, Freeze-Thaw Durable Sulphur Compositions, (1984)

← 1 2 →