LEAD ZIRCONATE-LEAD TITANATE PIEZOELECTRIC CERAMICS WITH IRON OXIDE ADDITIONS

被引:123
作者
WESTON, TB
WEBSTER, AH
MCNAMARA, VM
机构
[1] Mines Branch, Department of Energy
[2] Resources, Ottawa, Ontario
关键词
D O I
10.1111/j.1151-2916.1969.tb09178.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
An investigation of the effects of small additions of Fe2O3 to lead zirconate‐lead titanate ceramics with compositions between 45 and 60 mol% lead zirconate has shown that, with 2 moles of PbO to balance each mole of Fe2O3, the solubility of Fe2O3 was about 0.8 wt% in compositions near the tetragonal‐rhombohedra1 boundary. The dielectric constant and dissipation factor for both rhombohedra1 and tetragonal materials were decreased by addition of iron oxide, whereas the mechanical quality factor and frequency constant were increased. The dependence of the electromechanical properties on grain size was qualitatively similar for both undoped and iron oxide‐doped materials; the presence of iron oxide inhibited grain growth and lowered the limiting grain size below which the electromechanical properties change rapidly with grain size. Copyright © 1969, Wiley Blackwell. All rights reserved
引用
收藏
页码:253 / &
相关论文
共 15 条
[1]  
BARKLEY DJ, 1965, J CAN CERAM SOC, V34, P130
[2]   PREPARATION AND PROPERTIES OF SRTIL-XFEXO3-X/20X/2 SYSTEM [J].
BRIXNER, LH .
MATERIALS RESEARCH BULLETIN, 1968, 3 (04) :299-&
[3]   EFFECT OF FE-4+ IN THE SYSTEM SRFEO3-SRTIO3 [J].
CLEVENGER, TR .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1963, 46 (05) :207-210
[4]  
FULLMAN RL, 1953, T AM I MIN MET ENG, V197, P447
[7]  
MCNAMARA VM, 1965, J CAN CERAM SOC, V34, P103
[8]  
Murray T F, 1964, CERAM IND, V82, P74
[9]  
SUGDEN JA, 1962, Patent No. 3068177
[10]  
TANAKA Y, 1965, REV ELEC COMMUN LAB, V13, P744