EPOXY NETWORKS BASED ON DICYANDIAMIDE - EFFECT OF THE CURE CYCLE ON VISCOELASTIC AND MECHANICAL-PROPERTIES

被引:63
作者
AMDOUNI, N [1 ]
SAUTEREAU, H [1 ]
GERARD, JF [1 ]
PASCAULT, JP [1 ]
机构
[1] INST NATL SCI APPL,MAT MACROMOLEC LAB,CNRS,UA 507,BAT 403,F-69621 VILLEURBANNE,FRANCE
关键词
dicyandiamide; dynamic mechanical behaviour; epoxy-amine networks; glass transition; mechanical properties;
D O I
10.1016/0032-3861(90)90215-K
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Benzyldimethylamine-catalysed epoxy networks based on dicyandiamide hardener were prepared using various cure schedules. It was shown using 13C nuclear magnetic resonance and Fourier-transform infra-red spectroscopies that the chemical reactions are temperature-dependent. At low cure temperature the formation of ether linkages was favoured, thus increasing the crosslink density. Consequently, the glass transition temperature of the networks increases with decrease of the cure temperature. The viscoelastic spectra exhibited both α and β relaxations. The amplitude of the α peak increased with increasing cure temperature. Also the rubbery modulus allowed us to calculate M ̄c. The Young's moduli in the glassy state did not depend on the cure schedule. The ability to deform plastically determined both via K parameter and yield stress increases on decreasing the crosslink density, as shown with the high cure temperature. Linear elastic fracture mechanics allowed us to determine KIc and GIc. Both of the fracture parameters increased with decreasing crosslink density. The improvement in the retardation of crack propagation is probably due to a crack blunting mechanism associated with the ability of the material to deform plastically. © 1990.
引用
收藏
页码:1245 / 1253
页数:9
相关论文
共 36 条
[1]  
AMDOUNI N, IN PRESS
[3]   ON THE WORKHARDENING RATE OF GLASSY-POLYMERS .1. APPLICATION TO THE PHYSICAL AGING OF ATACTIC PMMA [J].
BULTEL, C ;
LEFEBVRE, JM ;
ESCAIG, B .
POLYMER, 1983, 24 (04) :476-480
[4]   INFLUENCE OF CHEMICAL-STRUCTURE ON NONELASTIC MECHANICAL-PROPERTIES IN POLYSTYRYL-PYRIDINE RESINS [J].
CAUX, X ;
COULON, G ;
ESCAIG, B .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 1987, 25 (10) :2189-2201
[5]   DYNAMIC RECOVERY AND EMBRITTLEMENT IN POLY(AMINOBISMALEIMIDE) [PABM] RESIN [J].
CAUX, X ;
COULON, G ;
ESCAIG, B .
POLYMER, 1986, 27 (11) :1749-1752
[6]   INFLUENCE OF THE DEGREE OF CROSSLINKING ON THE PLASTIC-DEFORMATION BEHAVIOR OF EPOXY-RESINS [J].
CAUX, X ;
COULON, G ;
ESCAIG, B .
POLYMER, 1988, 29 (05) :808-813
[7]  
Escaig B., 1982, PLASTIC DEFORMATION
[9]  
FISCHER M, 1988, 20TH EUR C MACR PHYS
[10]  
Flory P. J., 1953, PRINCIPLES POLYM CHE