SINTERING KINETICS AND MICROSTRUCTURE DEVELOPMENT OF NANOSCALE Y-TZP CERAMICS

被引:118
作者
THEUNISSEN, GSAM [1 ]
WINNUBST, AJA [1 ]
BURGGRAAF, AJ [1 ]
机构
[1] UNIV TWENTE,FAC CHEM TECHNOL,INORGAN CHEM MAT SCI & CATALYSIS LAB,POB 217,7500 AE ENSCHEDE,NETHERLANDS
关键词
D O I
10.1016/0955-2219(93)90031-L
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Zirconia samples doped with 3 mol% yttria were prepared by gel precipitation from a metal chloride solution and their sintering behaviour. compared with that of a commercial powder. Dense (relative density 97%) nanoscale ceramics with a mean grain size of 60 nm are obtained after sintering at 1050-degrees-C for 7 h. Important densification mechanisms in the initial sintering stage are grain boundary sliding and grain boundary diffusion. Grain growth in the final sintering stage seems to be impurity drag controlled. Extremely low activation energies are obtained for both densification and grain growth in the initial sintering stages. Special attention has been paid to the effect of aggregate size of the precursor powder on the final grain size.
引用
收藏
页码:315 / 324
页数:10
相关论文
共 38 条
[1]   DIFFUSION-ACCOMMODATED FLOW AND SUPERPLASTICITY [J].
ASHBY, MF ;
VERRALL, RA .
ACTA METALLURGICA, 1973, 21 (02) :149-163
[2]  
Birringer R., 1986, T JAPAN I METALS S, V2, P43
[3]  
BOUTZ MMR, 1990, SUPERPLASTICITY META, P87
[4]  
BOUTZ MMR, 1993, THESIS U TWENTE ENSC
[5]  
Brook RJ., 1976, TREATISE MAT SCI TEC, P331
[6]  
Claussen N., 1984, ADV CERAM, V12, P325
[7]  
DOLLIMORE D, 1964, J APPL CHEM, V14, P109
[8]   INFLUENCE OF AGGREGATES ON SINTERING [J].
DYNYS, FW ;
HALLORAN, JW .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1984, 67 (09) :596-601
[9]   SURFACE-AREA REDUCTION DURING ISOTHERMAL SINTERING [J].
GERMAN, RM ;
MUNIR, ZA .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1976, 59 (9-10) :379-383
[10]   SUPERPLASTICITY IN PURE ZRO2 [J].
HART, JL ;
CHAKLADER, AC .
MATERIALS RESEARCH BULLETIN, 1967, 2 (05) :521-+