GROWTH OF ZN(1-X)MN(X)SE AND ZN(1-X)FE(X)SE MIXED-CRYSTALS

被引：9

作者：

DEMIANIUK, M

机构：

[1] Institute of Technical Physics Lazurowa

来源：

MATERIALS RESEARCH BULLETIN | 1990年 / 25卷 / 03期

关键词：

D O I：

10.1016/0025-5408(90)90105-B

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Single crystals of (Zn,Mn)Se and (Zn,Fe)Se were grown by the modified Bridgman method under argon pressure. The value of x in Zn(1-x)Mn(x)Se was changed from 0 up to 0.53. Zn(1-1)Fe(x)Se crystals were grown with a concentration 0.01<x<0.22. The pressure during the growth process was 5.3±0.1 MPa. The mass losses during the crystallization process were less than 1 per cent. © 1990.

引用

页码：337 / 342

页数：6

共 11 条

[1] Demianiuk M., 1979, Electron Technology, V12, P91
[2] Demianiuk M., 1978, Electron Technology, V11, P79
[3] DEMIANIUK M, 1976, BIULETYN WAT, V25, P19
[4] FURDYNA JK, 1982, J APPL PHYS, V53, P8637
[5] PHYSICS AND APPLICATIONS OF II-VI-SEMIMAGNETICS
GALAZKA, RR
[J]. JOURNAL OF CRYSTAL GROWTH, 1985, 72 (1-2) : 364 - 370
[6] MICHALSKI E, 1982, ELECTRON TECHNOL, V13, P9
[7] Mycielski J., 1984, Progress in Crystal Growth and Characterization, V10, P101, DOI 10.1016/0146-3535(84)90025-X
[8] MAGNETIC-PROPERTIES OF ZN1-XMNXS
SWAGTEN, HJM
TWARDOWSKI, A
DEJONGE, WJM
DEMIANIUK, M
FURDYNA, JK
[J]. SOLID STATE COMMUNICATIONS, 1988, 66 (08) : 791 - 795
[9] SWAGTEN HJM, 1989, PHYS REV B, V39
[10] MAGNETIC-SUSCEPTIBILITY OF IRON-BASED SEMIMAGNETIC SEMICONDUCTORS - HIGH-TEMPERATURE REGIME
TWARDOWSKI, A
LEWICKI, A
ARCISZEWSKA, M
DEJONGE, WJM
SWAGTEN, HJM
DEMIANIUK, M
[J]. PHYSICAL REVIEW B, 1988, 38 (15): : 10749 - 10754

← 1 2 →