PHASE-DIAGRAM OF A NICKEL-ZINC FERRITE OF COMPOSITION NI0.685ZN0.177FE2.138O4+GAMMA

被引:5
作者
BRACCONI, P [1 ]
GALLAGHER, PK [1 ]
机构
[1] BELL TEL LABS INC,MURRAY HILL,NJ 07974
关键词
D O I
10.1111/j.1151-2916.1979.tb19047.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The oxygen content of Ni0.685Zn0.177Fe2.138O4+γ was determined gravimetrically at atmospheric pressure in varying Po2, 3.5 × 10−4 to 1.0 atm at 600° to 1450°C. The phase boundary associated with the precipitation of α‐Fe2O3 was determined from the change in slope of γ vs T plots observed on heating. Metastability is particularly evident for curves observed on cooling. Isacompositional lines (0.002 < γ < 0.045) are shown on a plot of log PO2 vs 1/T. An enthalpy of ‐21.6 kcal/mol is calculated for the oxidation of Fe2+. Copyright © 1979, Wiley Blackwell. All rights reserved
引用
收藏
页码:172 / 176
页数:5
相关论文
共 13 条
[1]  
BLANK JM, 1961, J APPL PHYS, V32, P378
[2]   KINETICS OF THE OXIDATION OF PLATINUM [J].
FRYBURG, GC ;
PETRUS, HM .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1961, 108 (06) :496-503
[3]  
Gallagher P.K., 1972, THERMOCHIM ACTA, V4, P283
[4]  
GALLAGHER PK, 1978, AM CERAM SOC BULL, V57, P576
[5]   AN INVESTIGATION OF THE PHASE COMPOSITIONS OF AN IRON-RICH NICKEL-ZINC FERROSPINEL [J].
JEFFERSON, CF ;
WESTRUM, EF .
JOURNAL OF PHYSICAL CHEMISTRY, 1957, 61 (10) :1430-1432
[6]   OXIDATION OF THE PLATINUM-GROUP METALS [J].
KRIER, CA ;
JAFFEE, RI .
JOURNAL OF THE LESS-COMMON METALS, 1963, 5 (05) :411-431
[7]   THERMOGRAVIMETRIC INVESTIGATION OF FE2P IN FERRITES CONTAINING EXCESS IRON [J].
MACKLEN, ED .
JOURNAL OF APPLIED PHYSICS, 1965, 36 (3P2) :1022-&
[8]   CHART OF PO2 VERSUS TEMPERATURE AND OXIDATION DEGREE FOR MN-ZN FERRITES IN COMPOSITION RANGE - 50 LESS-THAN FE2O3 LESS-THAN 54, 20 LESS-THAN MNO LESS-THAN 35, 11 LESS-THAN ZNO LESS-THAN 30 (MOLE PERCENT) [J].
MORINEAU, R ;
PAULUS, M .
IEEE TRANSACTIONS ON MAGNETICS, 1975, 11 (05) :1312-1314
[9]  
MORINEAU R, 1973, CR ACAD SCI C CHIM, V277, P437
[10]  
REIJNEN P, 1968, PHILIPS RES REP, V23, P151