CORROSION OF CARBON-STEELS, STAINLESS-STEELS, AND TITANIUM IN AQUEOUS LITHIUM BROMIDE SOLUTION

被引：66

作者：

GUINON, JL ^{[1
]}

GARCIAANTON, J ^{[1
]}

PEREZHERRANZ, V ^{[1
]}

LACOSTE, G ^{[1
]}

机构：

[1] ENSIGC,TOULOUSE,FRANCE

来源：

CORROSION | 1994年 / 50卷 / 03期

关键词：

CARBON STEEL; CHROMIUM; CORROSION; CURRENT DENSITY; INHIBITORS; LITHIUM BROMIDE; PH; PITTING; POLARIZATION RESISTANCE; POTENTIAL; STAINLESS STEEL; TEMPERATURE; TITANIUM; TYPE-316 STAINLESS STEEL; UNS G41350 STEEL; UNS R56400 ALLOY; WEIGHT LOSS;

D O I：

10.5006/1.3293516

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Effects of lithium bromide (LiBr) concentration pH temperature, exposure time, and the action of some inhibitors on corrosion of several carbon (C) steels, stainless steels (SS), and a titanium (Ti) alloy were studied Corrosion rates were determined by the polarization resistance method and compared to rates determined by weight-loss measurements. Pitting potentials (E(p)) were evaluated in neutral LiBr solution and with different inhibitors. Pit density and average pit depth depended on the metal tested, with lowest values for Ti, the next lowest values for type 316 SS (UNS S31600), and the highest values for UNS G41350 tempered steel

引用

页码：240 / 246

页数：7

共 21 条

[1] STRESS-CORROSION CRACKING REGIONS ON CONTOUR MAPS OF DISSOLUTION RATES FOR AISI 304 STAINLESS-STEEL IN SULFURIC-ACID-SOLUTIONS WITH CHLORIDE, BROMIDE, OR IODIDE
ASAWA, M
[J]. CORROSION, 1987, 43 (04) : 198 - 203
[2] Bard A.J., 1985, STANDARD POTENTIALS, P391
[3] THE INFLUENCE OF TEMPERATURE, APPLIED POTENTIAL, BUFFER AND INHIBITOR ADDITION ON THE PASSIVATION BEHAVIOR OF A COMMERCIAL GRADE 316L STEEL IN AQUEOUS HALIDE SOLUTIONS
CARROLL, WM
HOWLEY, MB
[J]. CORROSION SCIENCE, 1990, 30 (6-7) : 643 - 655
[4] DECHIALVO MRG, 1988, CORROS SCI, V28, P121, DOI 10.1016/0010-938X(88)90089-3
[5] Galvele J.R., 1978, PASSIVITY METALS, P285
[6] GRAYDON JW, 1990, CORROSION, V46, P1003
[7] PITTING SUSCEPTIBILITY OF STAINLESS-STEELS IN BROMIDE SOLUTIONS AT ELEVATED-TEMPERATURES
GUO, R
IVES, MB
[J]. CORROSION, 1990, 46 (02) : 125 - 129
[8] HEITZ E, 1986, PRINCIPLES ELECTROCH, P114
[9] Itoh M., 1990, BOSHOKU GIJUTSU, V39, P298
[10] Itoh M., 1989, BOSHOKU GIJUTSU, V38, P645

← 1 2 3 →