CONTINUING CRACK-TIP DEFORMATION AND FRACTURE FOR PLANE-STRAIN CRACK GROWTH IN ELASTIC-PLASTIC SOLIDS

Analysis of the deformation field consistent with a Prandtl stress distribution travelling with an advancing plane-strain crack reveals the functional form of the near tip crack profile in an elastic-plastic solid. The crack opening δ is shown to have the form δ ~ r In (const./r) at a distance r from the tip. This observation coupled with data generated from finite element investigations of growing cracks in small-scale yielding permits the construction of a relation characterizing the deformation at an extending crack tip. A ductile crack-growth criterion consisting of the attainment of a critical opening at a small characteristic material distance from the tip is adopted. Predictions of the stability of a growing crack for both small-scale yielding specimens and those subject to general yielding are discussed. © 1978.