LATERALLY LINKED MESOGENS IN MAIN CHAIN POLYMERS

The syntheses of liquid-crystalline main chain polyesters with laterally linked mesogens are presented. The terminal groups of the mesogens and the spacers fixation of mesogens, the polyesters with 1,4-di(p-alkoxybenzoyloxy)benzenes 1,4-di(p-alkoxybenzolyloxy)benzenes, 2,5-di(p-alkoxyphenyl)pyrimidines or a 4,4'-bis(p-ethoxyphenylazo)biphenyl derivative. Despite the unusual bilateral fixation of mesogens, the polyesters with 1,4-di(p-alkoxybenzoyloxy)benzenes show mainly monotropic phases which were found to be nematic in investigations with the polarizing microscope, in DSC measurements, temperature-dependent measurements of the Kerr constant and X-ray diffraction experiments. The monotropic nematic character remains when varying the terminal groups of the mesogen as well as the length of the n-alkanedioic acid spacer. However, when the spacer is branched, crystallization can be disturbed effectively and a stable nematic phase can be obtained. All of the polyesters with only 2,5-di(p-alkoxyphenyl)pyrimidines as mesogens are amorphous. The reason probably lies in the unsymmetric 4,6-substitution of the pyrimidine ring. In contrast to this, oligomers with a 4,4'-bis(p-ethoxyphenylazo)biphenyl derivative show broad, predominantly enantiotropic nematic phases with relatively high clearing temperatures. With the knowledge gained about relations between structure and properties, especially of polyesters with 1,4-(p-alkoxybenzoyloxy)benzenes as mesogens, polyesters with this mesogenic group but with various architectures have been compared. Speculations about possible arrangements of the structural elements have been included to explain the phase behaviour of the polyesters with laterally fixed mesogens.