CHANGES IN STRUCTURE AND ELECTRONIC-STATE FROM C-60 FULLERENE TO AMORPHOUS DIAMOND

被引:24
作者
HIRAI, H
KONDO, K
机构
[1] Research Laboratory of Engineering Materials, Tokyo Institute of Technology, Midori-ku, Yokohama 226
关键词
D O I
10.1103/PhysRevB.51.15555
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Changes in electronic state and structure from C60 fullerene to amorphous diamond under shock compression were examined by electron energy-loss spectroscopy and electron diffractometry for the recovered samples from the 50 to 55 GPa compressions. Three transient states were distinguished. In the first transient state, the fcc structure was almost unchanged, and the π plasmon was prohibited owing to decreasing intercluster distance. In the second state, the basic stacking structure of clusters was barely retained, and intercluster bondings were generated. In the third state, the fullerene structure collapsed to be amorphous, while sp3 bonding was partly produced. Finally, complete sp3 bonds were entirely reproduced, whereas the diamond structure in the long-range order was not reconstructed. © 1995 The American Physical Society.
引用
收藏
页码:15555 / 15558
页数:4
相关论文
共 21 条
[1]   EELS ANALYSIS OF VACUUM ARC-DEPOSITED DIAMOND-LIKE FILMS [J].
BERGER, SD ;
MCKENZIE, DR ;
MARTIN, PJ .
PHILOSOPHICAL MAGAZINE LETTERS, 1988, 57 (06) :285-290
[2]   EFFECTS OF PRESSURE AND STRESS ON C60 FULLERITE TO 20 GPA [J].
DUCLOS, SJ ;
BRISTER, K ;
HADDON, RC ;
KORTAN, AR ;
THIEL, FA .
NATURE, 1991, 351 (6325) :380-382
[3]   ANALYSIS OF CHEMICAL-VAPOR-DEPOSITED DIAMOND GRAIN-BOUNDARIES USING TRANSMISSION ELECTRON-MICROSCOPY AND PARALLEL ELECTRON-ENERGY-LOSS SPECTROSCOPY IN A SCANNING-TRANSMISSION ELECTRON-MICROSCOPE [J].
FALLON, PJ ;
BROWN, LM .
DIAMOND AND RELATED MATERIALS, 1993, 2 (5-7) :1004-1011
[4]   AMORPHOUS DIAMOND FROM C60 FULLERENE [J].
HIRAI, H ;
KONDO, K ;
YOSHIZAWA, N ;
SHIRAISHI, M .
APPLIED PHYSICS LETTERS, 1994, 64 (14) :1797-1799
[5]   QUENCHING A TRANSITION OF C-60 FULLERENE TO DIAMOND UNDER SHOCK COMPRESSION [J].
HIRAI, H ;
KONDO, KI ;
OHWADA, T .
CARBON, 1993, 31 (07) :1095-1098
[6]   MODIFIED PHASES OF DIAMOND FORMED UNDER SHOCK COMPRESSION AND RAPID QUENCHING [J].
HIRAI, H ;
KONDO, KI .
SCIENCE, 1991, 253 (5021) :772-774
[7]   NEW PHASES OF C-60 SYNTHESIZED AT HIGH-PRESSURE [J].
IWASA, Y ;
ARIMA, T ;
FLEMING, RM ;
SIEGRIST, T ;
ZHOU, O ;
HADDON, RC ;
ROTHBERG, LJ ;
LYONS, KB ;
CARTER, HL ;
HEBARD, AF ;
TYCKO, R ;
DABBAGH, G ;
KRAJEWSKI, JJ ;
THOMAS, GA ;
YAGI, T .
SCIENCE, 1994, 264 (5165) :1570-1572
[8]   CORE ELECTRON-EXCITATION SPECTRA OF DIAMOND, GRAPHITE, AND GLASSY-CARBON [J].
KOMA, A ;
MIKI, K .
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1984, 34 (01) :35-39
[9]   ELECTRON ENERGY-LOSS SPECTRA OF CARBON NANOTUBES [J].
KUZUO, R ;
TERAUCHI, M ;
TANAKA, M .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1992, 31 (10B) :L1484-L1487
[10]   HIGH-RESOLUTION ELECTRON ENERGY-LOSS SPECTRA OF SOLID-C-60 [J].
KUZUO, R ;
TERAUCHI, M ;
TANAKA, M ;
SAITO, Y ;
SHINOHARA, H .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1991, 30 (10B) :L1817-L1818