THE CORROSION BEHAVIOR OF NIOBIUM IN HYDROCHLORIC-ACID SOLUTIONS

被引:13
作者
COVINO, BS
CARTER, JP
CRAMER, SD
机构
关键词
D O I
10.5006/0010-9312-36.10.554
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A study of corrosion as a function of acid concentration, time, oxygen, and added ferric ion is reported. Weight loss tests were performed in air saturated (agitated and static) and helium saturated (agitated) hydrochloric acid solutions ranging from 1N to 10N at temperatures from 35 to 100 C and exposures up to 60 days.
引用
收藏
页码:554 / 558
页数:5
相关论文
共 17 条
[1]  
ACHERMAN WL, 1968, RI7169 US BUR MIN
[2]  
ACHERMAN WL, 1966, RI6715 US BUR MIN
[3]   ALLOYS AND REACTIVE METALS [J].
BADGER, FS .
INDUSTRIAL AND ENGINEERING CHEMISTRY, 1958, 50 (11) :1608-1611
[4]  
BARTON WR, 1962, IC8120 US BUR MIN
[5]  
EISELE JA, 1976, RI8188 US BUR MIN
[6]  
FONTANA MG, 1952, IND ENG CHEM, V44, pA71
[7]  
Hampel C.A., 1961, CORROSION, V17, P9
[8]  
JONES DO, 1961, CHEM PROCESSING AUG, P73
[9]  
KLINOV IY, 1971, P MOSCOW I CHEM MACH, V37
[10]  
LEE J, 1950, MATERIALS CONSTRUCTI