THE INFLUENCE OF ALLOYING ON THE MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF P/M NI3AL

被引:39
作者
WRIGHT, RN
KNIBLOE, JR
机构
[1] Idaho National Engineering Laboratory, EG and G Idaho, Inc., Idaho Falls
来源
ACTA METALLURGICA ET MATERIALIA | 1990年 / 38卷 / 10期
关键词
D O I
10.1016/0956-7151(90)90310-D
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The influence of alloying additions of iron and chromium alone and in combination with molybdenum and zirconium on the heat treatment response and mechanical properties of powder metallurgy processed Ni3Al based materials have been characterized. Additions of 8 at.% Cr result in considerable solid solution strengthening, while 11 at.% Fe by itself has little effect on the yield strength. Additions of both iron and chromium result in an alloy with higher strength than either unalloyed Ni3Al or alloys with either element alone, however, the ductility is reduced by formation of β′ phase. The alloys containing Fe or Cr alone and the unalloyed material are essentially single phase γ′ after heat treating at 1000°C for 1 h, while the more complex alloys have a significant volume fraction of disordered γ phase. The alloys with a high degree of order exhibit large yield drops and corresponding Lüders strains. As the amount of disorder increases the magnitude of both the yield drop and Lüders strain decreases. Values of the power law hardening exponent for the alloys are found to be as high as 0.8 and generally decrease as the amount of γ phase increases as a result of alloying. All of the materials have high strain rate sensitivity at elevated temperature combined with resistance to grain growth that suggests they will deform superplastically. © 1990.
引用
收藏
页码:1993 / 2001
页数:9
相关论文
共 31 条
[1]   IMPROVEMENT IN ROOM-TEMPERATURE DUCTILITY OF THE L12 TYPE INTERMETALLIC COMPOUND NI3A1 BY BORON ADDITION [J].
AOKI, K ;
IZUMI, O .
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1979, 43 (12) :1190-1196
[2]  
Besag F. M. C., 1970, Acta Metallurgica, V18, P429, DOI 10.1016/0001-6160(70)90128-8
[3]   LOAD RELAXATION STUDIES OF GRAIN-BOUNDARY EFFECTS IN 2 NI3AL ALLOYS AT ELEVATED-TEMPERATURES [J].
BLACK, R ;
CAROLAN, R ;
LI, CY ;
SIKKA, VK ;
LIU, CT .
SCRIPTA METALLURGICA, 1987, 21 (12) :1675-1680
[4]   CHARACTERISTICS OF NI3AL+FE POWDERS PRODUCED BY SPARK EROSION QUENCHING [J].
CAHN, RW ;
WALTER, JL ;
MARSH, DW .
MATERIALS SCIENCE AND ENGINEERING, 1988, 98 :33-37
[5]   THE ORDER-DISORDER TRANSFORMATION IN NI3AL AND NI3AL-FE ALLOYS .1. DETERMINATION OF THE TRANSITION-TEMPERATURES AND THEIR RELATION TO DUCTILITY [J].
CAHN, RW ;
SIEMERS, PA ;
GEIGER, JE ;
BARDHAN, P .
ACTA METALLURGICA, 1987, 35 (11) :2737-2751
[6]  
Edington J. W., 1976, PROG MATER SCI, V21, P61
[7]  
FLINN PA, 1969, T TMS AIME, V245, P1537
[8]   MICROSTRUCTURES AND MECHANICAL-PROPERTIES OF NI3AL ALLOYED WITH IRON ADDITIONS [J].
HORTON, JA ;
LIU, CT ;
SANTELLA, ML .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (07) :1265-1277
[9]   L12-TYPE NI-AL-CR ALLOYS PROCESSED BY RAPID SOLIDIFICATION [J].
HUANG, SC ;
HALL, EL ;
CHANG, KM ;
LAFORCE, RP .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (10) :1685-1692
[10]   MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF RAPIDLY QUENCHED L12 ALLOYS IN NI-AL-X SYSTEMS [J].
INOUE, A ;
TOMIOKA, H ;
MASUMOTO, T .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (07) :1367-1377