ELECTRICAL-CONDUCTIVITY OF NH2-SUBSTITUTED NI(II)-PHTHALOCYANINE

被引:12
作者
SIGNERSKI, R
KALINOWSKI, J
DAVOLI, I
STIZZA, S
机构
[1] CNR,IST FOTOCHIM & RADIAZ ALTA ENERGIA,I-40126 BOLOGNA,ITALY
[2] UNIV CAMERINO,DIPARTIMENTO MATEMAT & FIS,I-62032 CAMERINO,ITALY
来源
PHYSICA STATUS SOLIDI A-APPLIED RESEARCH | 1991年 / 125卷 / 02期
关键词
D O I
10.1002/pssa.2211250221
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
It is found that substitution of NH2 groups into positions 4, 4', 4", 4"' of Ni(II)-phthalocyanine (NH2-NiPc) transforms Ni(II)-phthalocyanine (NiPc) from a compound falling in the insulator (sigma almost-equal-to 10(-12) OMEGA-1 cm-1) to semiconductor (sigma almost-equal-to 10(-4) OMEGA-1 cm-1) range of electrical conductivities. The change in the conductivity reaches about 8 orders of magnitude, being dependent on the ambient conditions. The samples of NH2-NiPc exposed to air show up to 3 orders of magnitude higher conductivity than those examined immediately after evaporation under vacuum almost-equal-to 10(-3) Pa. Surface-and sandwich-mode conductivity measurements are performed showing similar activation energies of the current within the range 0.05 to 1.0 eV dependent on the temperature range and the ambient. Applying Auger spectroscopy NH2-NiPc is found to contain over 50% more oxygen than NiPc. It is, therefore, suggested that the larger conductivity of NH2-NiPc is due to its greater ability to absorb oxygen. Possible reasons of this property are discussed, the more open crystal structure, as one of them, is confirmed by separated XANES studies of the local structure at Ni atom in both the compounds. The temperature behaviour of the conductivity of NH2-NiPc under vacuum is discussed in terms of an interplay between electrode injection and bulk-generated carriers contributing to the measured current, the injection dominating at low temperatures.
引用
收藏
页码:597 / 607
页数:11
相关论文
共 29 条
[1]   SYNTHESIS AND STRUCTURAL STUDIES OF METAL(II) 4,9,16,23-PHTHALOCYANINE TETRAAMINES [J].
ACHAR, BN ;
FOHLEN, GM ;
PARKER, JA ;
KESHAVAYYA, J .
POLYHEDRON, 1987, 6 (06) :1463-1467
[2]   ELECTRON TRAPPING AND BULK CONDUCTION IN BETA-FORM METAL-FREE PHTHALOCYANINE SINGLE CRYSTALS IN VACUUM [J].
BARBE, DF ;
WESTGATE, CR .
SOLID STATE COMMUNICATIONS, 1969, 7 (07) :563-&
[3]   BULK TRAPPING STATES IN BETA-PHTHALOCYANINE SINGLE CRYSTALS [J].
BARBE, DF ;
WESTGATE, CR .
JOURNAL OF CHEMICAL PHYSICS, 1970, 52 (08) :4046-+
[4]   DRIFT MOBILITY, TRAPPING AND PHOTOGENERATION OF CHARGE-CARRIERS IN BETA-METAL-FREE PHTHALOCYANINE SINGLE-CRYSTALS [J].
COX, GA ;
KNIGHT, PC .
JOURNAL OF PHYSICS C-SOLID STATE PHYSICS, 1974, 7 (01) :146-156
[5]  
CURRY J, 1962, J CHEM PHYS, V57, P2154
[6]   ELECTRON INJECTION IN THIN FILMS OF COPPER PHTALOCYANINE [J].
DELACOTE, GM ;
FILLARD, JP ;
MARCO, FJ .
SOLID STATE COMMUNICATIONS, 1964, 2 (12) :373-376
[7]   ELECTRICAL PROPERTIES OF POLY-COPPER PHTHALOCYANINE [J].
EPSTEIN, A ;
WILDI, BS .
JOURNAL OF CHEMICAL PHYSICS, 1960, 32 (02) :324-329
[8]   ASYMMETRIES IN THE OPTICAL-PROPERTIES OF VACUUM-DEPOSITED ORGANIC FILMS ILLUMINATED AT THE SUBSTRATE AND NONSUBSTRATE SURFACES [J].
GODLEWSKI, J ;
KALINOWSKI, J ;
STIZZA, S ;
DAVOLI, I ;
BERNARDINI, R .
THIN SOLID FILMS, 1987, 146 (02) :115-132
[9]   DEPENDENCE OF THE MOBILITY AND TRAP CONCENTRATION IN EVAPORATED COPPER PHTHALOCYANINE THIN-FILMS ON BACKGROUND PRESSURE AND EVAPORATION RATE [J].
GOULD, RD .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1986, 19 (09) :1785-1790
[10]  
HAMMANN C, 1978, ORGANISCHE FESTKORPE