MATRIX CRACKING AND THE MECHANICAL-BEHAVIOR OF SIC-CAS COMPOSITES

An experimental investigation has been carried out on the mechanical properties of unidirectional (0)12, (0, 90)3s, (+/- 45, 0(2))s, and (+/- 45)3s composites consisting of CAS glass ceramic reinforced with Nicalon SiC fibres. Measurements have been made of the elastic properties and of the tensile, compression and shear strengths of the composites, and these have been supported by a detailed study of the damage which occurs during monotonic and repeated loading. These damage studies have been carried out by means of edge replication microscopy and acoustic emission monitoring. The elastic properties of the composites are, by and large, close to the values that would be predicted from the constituent properties and lay-up sequences, but their strengths are lower than expected, and it appears that the Nicalon reinforcing fibre has been seriously degraded during manufacture. The fracture energy is much higher than predicted from observations of fibre pull-out, and it is suggested that the energy required to form a close three-dimensional network of matrix cracks could account for the high apparent toughness. The matrix cracking stress can be predicted reasonably closely by the Aveston, Cooper and Kelly model of cracking in brittle matrix composites, but it is shown that subcritical microcracks can form and/or grow at stresses well below the predicted critical values without affecting composite properties.