ADHESION OF POLYETHYLENE TO METALS - ROLE OF SURFACE-TOPOGRAPHY

Previous work established the importance of the fibrous substrate topography in obtaining good adhesion of polyethylene to matt black oxide films formed on copper in alkaline solution. In this paper the effect of the very rough surface topography is shown to be general. Anodising treatments for copper and zinc and a high temperature oxidation for steel are described which give a very rough surface consisting (respectively) of fibrous, dendritic and blade-like growths. The peel strength of polyethylene to these substrates is high even under circumstances, for example when the polymer is stabilised with antioxidant, where adhesion to a chemically similar smooth surface is low. The high peel strength is associated with large amounts of energy being dissipated during peeling in plastic deformation of the polymer near the interface. It is suggested that this is caused by the development of high shear stress concentration at the fibre ends causing yielding in a large volume of polymer. © 1979, Taylor & Francis Group, LLC. All rights reserved.