ELECTROPHORETIC DEPOSITION OF TL-BA-CA-CU-O AND BI2SR2CACU2OX THICK-FILMS

被引：5

作者：

REMILLARD, SK ^{[1
]}

ARENDT, PN ^{[1
]}

ELLIOTT, NE ^{[1
]}

机构：

[1] UNIV CALIF LOS ALAMOS SCI LAB,LOS ALAMOS,NM 87545

来源：

PHYSICA C | 1991年 / 177卷 / 4-6期

关键词：

SURFACE-RESISTANCE; SUPERCONDUCTORS; GROWTH;

D O I：

10.1016/0921-4534(91)90489-L

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Thick films of Bi-2212 and Tl-2212 superconductor were electrophoretically deposited onto Consil substrates. Tl series starting powder containing BaCuO2 impurity phase resulted in films with igher Tl content. X-ray diffraction showed that Bi-2212 films were well oriented only if melt textured. Melt textured Bi-2212 films were characterized in a TE011 resonant cavity at 17.46 GHz and compared to a magnetron sputtered Tl-2212 thick film. It was found that the surface resistance and surface reactance of the Bi-2212 were equally sensitive to external DC magnetic fields.

引用

页码：345 / 350

页数：6

共 21 条

[11] IMPROVEMENT IN CRITICAL CURRENT-DENSITY OF BI2SR2CA1CU2OX TAPES SYNTHESIZED BY DOCTOR-BLADE CASTING AND MELT GROWTH [J].