INFLUENCE OF HYDROGEN ON INTERNAL FRICTION OF NICKEL

被引：4

作者：

COMBETTE, P

PEREZ, J

GOBIN, P

机构：

[1] Centre d'Etudes Nucléaires

[2] Département de Physique, Institut National des Sciences Appliquées, Lyon

来源：

JOURNAL OF PHYSICS D-APPLIED PHYSICS | 1968年 / 1卷 / 08期

关键词：

D O I：

10.1088/0022-3727/1/8/418

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Hydrogen modifies the internal friction of zone-refined nickel: specimens without hydrogen have high internal friction, due mainly to the movement of dis-locations, whereas specimens with hydrogen have low internal friction which rises after cold working and then decreases as the temperature increases. The results presented are compatible with the idea of pinning of dislocations by hydrogen.

引用

页码：1075 / &

共 20 条

[11]

HERMANT ME, 1966, THESIS U AMSTERDAM

[12]

HERMANT ME, J PHYSIQUE S, V27, P209

[13]

HERMANT ME, ACTA METALL, V14, P795

[14] ETUDE DU NICKEL HYDROGENE [J].

LETEURTRE, J .

JOURNAL DE PHYSIQUE, 1966, 27 (7-8S) :109-+

[15] CONTINUOUS RECORDING OF DAMPING AT CONSTANT AMPLITUDE [J].

PEREZ, J ;

DELORME, J ;

PEGUIN, P ;

GOBIN, P .

JOURNAL OF SCIENTIFIC INSTRUMENTS, 1967, 44 (02) :169-&

[16] DAMPING PEAKS IN DEFORMED NICKEL [J].

SOMMER, AW ;

BESHERS, DN .

JOURNAL OF APPLIED PHYSICS, 1966, 37 (13) :4603-+

[17]

TETELMAN AS, 1963, FRACTURE SOLIDS, P671

[18]

VANNESTE A, 1963, THESIS U LAVAL

[19] THE EFFECTS OF AGING AND STRAINING ON THE INTERNAL FRICTION OF HYDROGEN CHARGED 1020 STEEL AT LOW TEMPERATURES [J].

WEINER, LC ;

GENSAMER, M .

ACTA METALLURGICA, 1957, 5 (12) :692-694

[20] INTERCRYSTALLINE FRACTURE IN HYDROGEN-CHARGED NICKEL [J].

WILCOX, BA ;

SMITH, GC .

ACTA METALLURGICA, 1965, 13 (03) :331-&

← 1 2 →