SINTERING OF POWDERS OF POLYAROMATIC MESOPHASE TO HIGH-STRENGTH ISOTROPIC CARBONS .1. INFLUENCE OF THE RAW-MATERIAL AND SINTERING CONDITIONS ON THE PROPERTIES OF THE CARBON MATERIALS

被引:53
作者
HOFFMANN, WR
HUTTINGER, KJ
机构
[1] Institut für Chemische Technik der Universität Karlsruhe, 76128 Karlsruhe
关键词
MESOPHASE; PARTICLE SIZE; SINTERING; HIGH-TEMPERATURE TREATMENT; FINE-GRAINED CARBONS;
D O I
10.1016/0008-6223(94)90218-6
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The sintering of compacted mesophase powders of varying nature and particle size was studied. The sintered carbons were stepwise heat-treated to 2600-degrees-C, and their properties were determined after each step. The sintering process is composed of a transient liquid-phase sintering step and a subsequent reaction sintering step in the solid state. The investigation of both process steps and the properties of the heat-treated carbons indicate that the initial transient liquid-phase sintering is the decisive step, and thus predetermines the properties of the heat-treated carbons. After graphitization treatment of sintered carbons at 2400-degrees-C, flexural strength values up to 160 MPa were obtained. Criteria for the selection of the mesophase, the particle size, and the sintering conditions are discussed.
引用
收藏
页码:1087 / 1103
页数:17
相关论文
共 50 条
  • [21] Hoffmann W.R., 1991, THESIS U KARLSRUHE
  • [22] MODELING OF THE APPARENT VISCOSITY OF PITCHES AND MESOPHASES AT LINEAR TEMPERATURE INCREASE UP TO 500-DEGREES-C
    HOFFMANN, WR
    HUTTINGER, KJ
    [J]. CARBON, 1993, 31 (02) : 263 - 268
  • [23] DEMONSTRATION OF SPONTANEOUS LIQUID-PHASE SINTERING OF MESOPHASE POWDERS
    HOFFMANN, WR
    HUTTINGER, KJ
    [J]. CARBON, 1993, 31 (02) : 259 - 262
  • [24] HOFFMANN WR, 1992, P CARBON 92 ESSEN, P126
  • [25] HOFFMANN WR, 1992, P CARBON 92 ESSEN, P129
  • [26] HUTTNER W, 1991, ERDOL KOHLE ERDGAS, V107, P81
  • [27] JAGER H, 1988, P CARBON 88 NEWCASTL, P58
  • [28] JANOSCHEK, 1979, THESIS U KARLSRUHE
  • [29] GRAPHITIZATION OF PITCH COKE - CHANGES IN MEAN INTERLAYER SPACING, STRAIN AND WEIGHT
    KAWAMURA, K
    BRAGG, RH
    [J]. CARBON, 1986, 24 (03) : 301 - 309
  • [30] KITAJIMA E, 1985, 17 BIENN C CARB LEX, P460