OPTICAL-PROPERTIES OF LINBO3 IMPLANTED WITH AG+ IONS

被引：32

作者：

SHANG, DY

SAITO, Y

SUGANOMATA, S

机构：

[1] Yamanashi University, Kofu, 400

来源：

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS | 1994年 / 33卷 / 7A期

关键词：

ION IMPLANTATION; SURFACE MODIFICATION; COLORATION; LINBO3; SMALL PARTICLES OF AG; ABSORPTION SPECTRUM;

D O I：

10.1143/JJAP.33.L966

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Ag+ ions were implanted into LiNbO3 held at room temperatures with the energy of 25 keV in the range of 2 X 10(15) to 8 X 10(16) ions/cm2. Absorption in the visible range was measured. LiNbO3 implanted with Ag+ ions shows brilliant reddish-violet and a large absorption peak at about 520 nm. Ag atoms aggregate during implantation and form very small flat particles of the size of about 0.3 to a few micrometers in surface layers of depths up to 16 nm.

引用

收藏

页码：L966 / L969

页数：4

相关论文

共 18 条

[1] NEAR-SURFACE NUCLEATION AND CRYSTALLIZATION OF AN ION-IMPLANTED LITHIA-ALUMINA-SILICA GLASS [J].

ARNOLD, GW .

JOURNAL OF APPLIED PHYSICS, 1975, 46 (10) :4466-4473

[2] AGGREGATION AND MIGRATION OF ION-IMPLANTED SILVER IN LITHIA-ALUMINA-SILICA GLASS [J].

ARNOLD, GW ;

BORDERS, JA .

JOURNAL OF APPLIED PHYSICS, 1977, 48 (04) :1488-1496

[3] QUANTUM CONFINEMENT IN SI NANOCRYSTALS [J].

DELLEY, B ;

STEIGMEIER, EF .

PHYSICAL REVIEW B, 1993, 47 (03) :1397-1400

[4] ABSORPTION OF LIGHT BY COLLOIDS IN ALKALI HALIDE CRYSTALS [J].

DOYLE, WT .

PHYSICAL REVIEW, 1958, 111 (04) :1067-1072

[5]

FUKMI T, 1993, REIZA KENKYU, V21, P1151

[6] AU+-ION-IMPLANTED SILICA GLASS WITH NONLINEAR OPTICAL PROPERTY [J].

FUKUMI, K ;

CHAYAHARA, A ;

KADONO, K ;

SAKAGUCHI, T ;

HORINO, Y ;

MIYA, M ;

HAYAKAWA, J ;

SATOU, M .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1991, 30 (4B) :L742-L744

[7] OBSERVATION OF THE ENHANCED INFRARED-ABSORPTION OF PARA-NITROBENZOATE ON AG ISLAND FILMS WITH AN ATR TECHNIQUE [J].

HATTA, A ;

OHSHIMA, T ;

SUETAKA, W .

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1982, 29 (02) :71-75

[8] PHOTOLUMINESCENCE OF SI-RICH SIO2-FILMS - SI CLUSTERS AS LUMINESCENT CENTERS [J].

HAYASHI, S ;

NAGAREDA, T ;

KANZAWA, Y ;

YAMAMOTO, K .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1993, 32 (9A) :3840-3845

[9]

Kubodera K., 1993, Review of Laser Engineering, V21, P1078, DOI 10.2184/lsj.21.11_1078

[10] VISIBLE PHOTOLUMINESCENCE OF GE MICROCRYSTALS EMBEDDED IN SIO2 GLASSY MATRICES [J].

MAEDA, Y ;

TSUKAMOTO, N ;

YAZAWA, Y ;

KANEMITSU, Y ;

MASUMOTO, Y .

APPLIED PHYSICS LETTERS, 1991, 59 (24) :3168-3170