SYNTHESIS AND CHARACTERIZATION OF COPOLYMERS BASED ON 2-VINYLPYRIDINE AND DIVINYLBENZENE

被引:18
作者
COUTINHO, FMB
SIQUEIRA, MIN
BARBOSA, CR
机构
[1] Instituto de Macromoléculas, Universidade Federal do Rio de Janeiro, Rio de Janeiro, RJ 21945
关键词
D O I
10.1016/0014-3057(90)90026-Z
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Macroporous and gel-type anion exchange resins were synthesized in a suspension copolymerization of 2-vinylpyridine with divinylbenzene in the presence of methyl ethyl ketone and n-heptane as diluents. The effects of diluents and crosslinking degree on the properties of these matrices were studied. It was found that 60% of heptane in the diluent mixture always leads to macroporous resins whatever the crosslinking degree. The resins were evaluated in terms of structure porosity, specific area and ion exchange capacity. © 1990.
引用
收藏
页码:1189 / 1193
页数:5
相关论文
共 16 条
[11]  
Millar JR, 1965, J CHEM SOC, V304
[12]   STYRENE-DIVINYLBENZENE COPOLYMERS .7. STABILITY OF THE POROUS STRUCTURES FORMED IN TOLUENE CYCLOHEXANOL MIXTURES [J].
OKAY, O .
ANGEWANDTE MAKROMOLEKULARE CHEMIE, 1988, 157 :15-21
[13]   ON THE STRUCTURE OF MACRORETICULAR STYRENE-DIVINYLBENZENE COPOLYMERS [J].
POINESCU, I ;
VLAD, C ;
CARPOV, A ;
IOANID, A .
ANGEWANDTE MAKROMOLEKULARE CHEMIE, 1988, 156 :105-121
[14]   STYRENE-DIVINYLBENZENE COPOLYMERS - INFLUENCE OF THE DILUENT ON NETWORK POROSITY [J].
POINESCU, IC ;
BELDIE, C ;
VLAD, C .
JOURNAL OF APPLIED POLYMER SCIENCE, 1984, 29 (01) :23-34
[15]   STYRENE-DIVINYLBENZENE COPOLYMERS - CONSTRUCTION OF POROSITY IN STYRENE DIVINYLBENZENE MATRICES [J].
SEDEREL, WL ;
DEJONG, GJ .
JOURNAL OF APPLIED POLYMER SCIENCE, 1973, 17 (09) :2835-2846
[16]   SELECTIVE METAL SORPTION ON CROSS-LINKED POLY(VINYLPYRIDINE) RESINS [J].
SUGII, A ;
OGAWA, N ;
IINUMA, Y ;
YAMAMURA, H .
TALANTA, 1981, 28 (08) :551-556