In order to study the relation between the scatter characteristics of small crack growth behaviour and fatigue life, rotatory bending fatigue tests of smooth specimens were carried out using 0.21% carbon steels of different ferrite grain sizes. Fifteen to eighteen specimens were fatigued at each stress amplitude, and the initiation and propagation behaviour of the cracks which led to the final fractures were examined for all the specimens. The physical basis of scatter in fatigue life was investigated, based on the successive observation of fatigue damage on the surface using the plastic replica technique, followed by an analysis of the data assuming a Weibull distribution, A statistical investigation of the physical basis of scatter in relation to the ferrite grain size was performed, i.e. the distributions for crack initiation life, crack propagation life, fatigue life and growth rate of small cracks. Finally, the fluctuation of crack growth rate was studied in relation to the application of a crack growth law for microstructurally small cracks.