POSITIVE EXPONENT SUPERPLASTICITY IN ADVANCED ALUMINUM-ALLOYS WITH NANO OR NEAR-NANO SCALE GRAINED STRUCTURES

被引:85
作者
HIGASHI, K
机构
[1] Department of Mechanical Engineering, University of Osaka Prefecture, Sakai, Osaka, 593, Gakuen-cho
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1993年 / 166卷 / 1-2期
关键词
D O I
10.1016/0921-5093(93)90315-6
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Very high strain rate superplasticity was observed in near-nano scale aluminum alloys. These alloy systems include the group of mechanically alloyed IN9021, IN90211, IN9052, IN905XL alloys and SiCp/IN9021 composite, an Al-14wt.%Ni-14wt.%Mm (Mm is mischmetal) crystalline alloy consolidated from its amorphous powders and an Al-14wt.%Ni-7wt.%Mm-1wt.%Zr alloy consolidated from nanocrystalline powders, and an Al-7wt.%Cr-1wt.%Fe alloy produced by physical vapor deposition. In each of the above advanced alloy systems, large elongations of more than 500% were obtained at extremely high strain rates of more than 1 s-1 (called positive exponent superplasticity). In the mechanical alloyed IN9021 aluminum alloy with a fine grained structure 500 nm in size, a maximum elongation of 1250% was recorded at an extremely high strain rate of 50 s-1 at 823 K. In addition, a maximum elongation of 610% was obtained at a very high strain rate of 5 s-1 of 823 K in the mechanically alloyed 15vol.%SiCp/IN9021 aluminum composite. A maximum elongation of 650% was observed at a high strain rate of 1 s-1 in both Al-Ni-Mm and Al-Ni-Mm-Zr alloys consolidated from amorphous or nanocrystalline powders. Also a maximum elongation of 505% was obtained at a high strain rate of 1 s -1 in a VQ Al-Cr-Fe alloy.
引用
收藏
页码:109 / 118
页数:10
相关论文
共 12 条
  • [1] SUPERPLASTIC-LIKE BEHAVIOR AT HIGH-STRAIN RATES IN MECHANICALLY ALLOYED ALUMINUM
    BIELER, TR
    NIEH, TG
    WADSWORTH, J
    MUKHERJEE, AK
    [J]. SCRIPTA METALLURGICA, 1988, 22 (01): : 81 - 86
  • [2] Gardiner R., 1987, MET MATER, V3, P254
  • [3] SUPERPLASTIC BEHAVIOR IN A MECHANICALLY ALLOYED ALUMINUM COMPOSITE REINFORCED WITH SIC PARTICULATES
    HIGASHI, K
    OKADA, T
    MUKAI, T
    TANIMURA, S
    NIEH, TG
    WADSWORTH, J
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (02): : 185 - 190
  • [4] POSITIVE EXPONENT STRAIN-RATE SUPERPLASTICITY IN MECHANICALLY ALLOYED ALUMINUM IN9021
    HIGASHI, K
    OKADA, T
    MUKAI, T
    TANIMURA, S
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (09): : 2053 - 2057
  • [5] HIGH-STRAIN RATE SUPERPLASTICITY IN AN AL-NI-MISCH METAL ALLOY PRODUCED FROM ITS AMORPHOUS POWDERS
    HIGASHI, K
    MUKAI, T
    TANIMURA, S
    INOUE, A
    MASUMOTO, T
    KITA, K
    OHTERA, K
    NAGAHORA, J
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (02): : 191 - 196
  • [6] SUPERPLASTIC BEHAVIOR AT HIGH-STRAIN RATES OF A MECHANICALLY ALLOYED AL-MG-LI ALLOY
    HIGASHI, K
    OKADA, T
    MUKAI, T
    TANIMURA, S
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (05): : 761 - 766
  • [7] VERY HIGH-STRAIN RATE SUPERPLASTICITY IN A MECHANICALLY ALLOYED IN9052 ALUMINUM-ALLOY
    HIGASHI, K
    OKADA, T
    MUKAI, T
    TANIMURA, S
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1992, 159 (01): : L1 - L4
  • [8] AL-Y-NI AMORPHOUS POWDERS PREPARED BY HIGH-PRESSURE GAS ATOMIZATION
    INOUE, A
    KITA, K
    OHTERA, K
    KIMURA, H
    MASUMOTO, T
    [J]. JOURNAL OF MATERIALS SCIENCE LETTERS, 1988, 7 (12) : 1287 - 1290
  • [9] NAGAHAMA H, 1993, IN PRESS PHILOS MAG, V67
  • [10] EXTENDED DUCTILITY AT HIGH-STRAIN RATES IN A MECHANICALLY ALLOYED ALUMINUM-ALLOY
    NIEH, TG
    GILMAN, PS
    WADSWORTH, J
    [J]. SCRIPTA METALLURGICA, 1985, 19 (11): : 1375 - 1378