THERMOGRAVIMETRIC STUDY OF THE REDUCTION STEP IN ND1.85CE0.15CU1.01OY AS A FUNCTION OF THE OXYGEN PARTIAL-PRESSURE

被引：16

作者：

PRADO, F

CANEIRO, A

SERQUIS, A

BRIATICO, J

机构：

[1] Centro Atómico Bariloche, CNEA, Bariloche

来源：

SOLID STATE COMMUNICATIONS | 1995年 / 94卷 / 01期

关键词：

HIGH T-C SUPERCONDUCTORS; THERMODYNAMIC PROPERTIES;

D O I：

10.1016/0038-1098(94)00844-2

中图分类号：

O469 [凝聚态物理学];

学科分类号：

070205 [凝聚态物理];

摘要：

Thermodynamic measurements of the equilibrium oxygen partial pressure as a function of the oxygen content have been performed in Nd1.85Ce0.15Cu1.01Oy at 900 degrees C. These measurement suggest the presence of two kinds of defects: interstitial oxygen atoms for PO2 higher than the one corresponding to the thermodynamic equilibrium CuO-Cu2O (1.4 x 10(-2) atm) and oxygen vacancies for oxygen partial pressure below this value. The superconducting transition of samples with controlled oxygen content was studied through Magnetically Modulated Microwave Absorption (MaMMA). The superconducting transition was observed only for samples quenched at PO2 lower than 1.4x10(-2) atm. These results confirm that in order to obtain superconductivity in this material interstitial oxygen atoms must be removed from its structure.

引用

页码：75 / 80

页数：6

共 22 条

[1]

THERMODYNAMIC STUDY ON OXIDE CEO(2-X) FOR 1.5 LESS-THAN O/CE LESS-THAN 2 [J].