CRYSTALLIZATION OF SPUTTERED LEAD ZIRCONATE TITANATE FILMS BY RAPID THERMAL-PROCESSING

被引:119
作者
KUMAR, CVRV
PASCUAL, R
SAYER, M
机构
[1] Department of Physics, Queen's University, Kingston
关键词
D O I
10.1063/1.351307
中图分类号
O59 [应用物理学];
学科分类号
摘要
A rapid thermal annealing (RTA) technique has been employed to process lead zirconate titanate (PZT) films prepared by reactive magnetron sputtering. The films were fabricated by dc sputtering a multielement metal target in an oxygen ambient at a substrate temperature of 200-degrees-C. A subsequent postdeposition RTA at 600-degrees-C for 5 s crystallizes the films into a perovskite-type structure through various intermediate phases. Due to the short postdeposition processing times inherent in the RTA method, the initial nature of the asgrown films has a critical influence on the crystallization kinetics. The reaction sequence in the formation of perovskite PZT from the films deposited at low substrate temperatures by the sputtering technique has been evaluated, and various key factors influencing the crystallization of PZT have been identified. As-grown films are constituted of polycrystalline orthorhombic lead oxide in an amorphous matrix of titania and zirconia. During annealing lead oxide transforms into a cubic phase, and the lead oxide stoichiometry determines the processing route to PZT. In the case of lead-rich films, intermediate compounds of lead with titania and zirconia are observed, which react during the final stage of annealing at 600-degrees-C to form PZT. In lead-deficient films, the formation of a pyrochlore phase has been observed, which crystallizes into perovskite at 750-degrees-C. The Zr/Ti ratio also influences the crystallization sequence. In the case of Ti-rich PZT, the intermediate compounds initially involve a zirconium-rich rhombohedral PZT, with which residual titanium reacts to form tetragonal PZT. The films showed good ferroelectric and other electrical properties with a remanent polarization of 24-mu-C/cm2, coercive field of 32 kV/cm, epsilon' = 950, tan delta = 0.02, and sigma(dc) (300 K) = 10(-12) OMEGA-1 cm-1 with an activation energy between 0.9 and 1.4 eV.
引用
收藏
页码:864 / 874
页数:11
相关论文
共 81 条
[11]  
Budd K. D., 1985, British Ceramic Proceedings, P107
[12]  
CARRANO J, 1989, IEEE IEDM, V89, P255
[13]   ION-BEAM DEPOSITION OF THIN-FILMS OF FERROELECTRIC LEAD ZIRCONATE TITANATE (PZT) [J].
CASTELLANO, RN ;
FEINSTEIN, LG .
JOURNAL OF APPLIED PHYSICS, 1979, 50 (06) :4406-4411
[14]   REACTION-MECHANISMS IN THE FORMATION OF PZT SOLID-SOLUTIONS [J].
CHANDRATREYA, SS ;
FULRATH, RM ;
PASK, JA .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (07) :422-425
[15]   POLYMORPHIC PHASE-TRANSFORMATION OF LEAD MONOXIDE AND ITS INFLUENCE ON LEAD ZIRCONATE TITANATE FORMATION [J].
CHEN, SY ;
CHENG, SY ;
WANG, CM .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (02) :232-236
[16]  
CHIANG CK, 1990, FERROELECTRIC THIN F, V200, P133
[17]   ELECTRICAL-CONDUCTIVITY IN LEAD ZIRCONATE-TITANATE CERAMICS [J].
DIH, JJ ;
FULRATH, RM .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1978, 61 (9-10) :448-451
[18]   GROWTH AND PROPERTIES OF PIEZOELECTRIC AND FERROELECTRIC-FILMS [J].
FRANCOMBE, MH ;
KRISHNASWAMY, SV .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1990, 8 (03) :1382-1390
[19]   ASYMMETRIC HYSTERESIS LOOPS OF FERROELECTRIC PZT FILM [J].
FUKAMI, T ;
FUJII, S .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1985, 24 (05) :632-633
[20]  
FUKAMI T, 1983, ELECTR ENG JPN, V103, P15