STUDY OF PASSIVE FILM FORMATION ON CU-NI 70/30 ALLOY IN SEAWATER AT HIGH-TEMPERATURE

被引:18
作者
BECCARIA, AM
WANG, YZ
POGGI, G
机构
[1] Istituto Per la Corrosione Marina Dei Metalli, Cnr, Genova, 16149
关键词
D O I
10.1002/sia.740210621
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The corrosion mechanism of Cu-Ni 70/30 alloy in quiescent seawater at 80-degrees-C with a dissolved oxygen content of 3.0 ppm was studied with electrochemical and free corrosion tests. The passive films formed on free corroded specimens after an exposure time of 10 min-360 h were analysed with XPS. Free corrosion tests show that Cu-Ni alloy undergoes copper-selective dissolution; the kinetics of the dissolution process are governed by a transport-limited mechanism. Electrochemical tests show that the overall corrosion process is under cathodic control and that the reduction of dissolved oxygen is the most important parameter of the corrosion process. X-ray photoelectron spectroscopy shows that the composition of the passive films changes by changing the exposure time. The main components of the passive films formed on metallic surfaces are Ni compounds after the shorter exposure time and Cu compounds after a longer exposure time.
引用
收藏
页码:442 / 446
页数:5
相关论文
共 37 条
[1]   ANODIC DISSOLUTION OF COPPER IN FLOWING SODIUM-CHLORIDE SOLUTIONS BETWEEN 25 DEGREES AND 175 DEGREES C [J].
BACARELLA, AL ;
GRIESS, JC .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1973, 120 (04) :459-465
[2]   CORROSION OF CONDENSER TUBE ALLOYS IN SULFIDE CONTAMINATED BRINE [J].
BATES, JF ;
POPPLEWELL, JM .
CORROSION, 1975, 31 (08) :269-275
[3]   H2O INTERACTION WITH CLEAN AND OXYGEN PRECOVERED NI(110) [J].
BENNDORF, C ;
NOBL, C ;
RUSENBERG, M ;
THIEME, F .
SURFACE SCIENCE, 1981, 111 (01) :87-101
[4]   AN ELLIPSOMETRIC DETERMINATION OF MECHANISM OF PASSIVITY OF NICKEL [J].
BOCKRIS, JO ;
REDDY, AKN ;
RAO, B .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1966, 113 (11) :1133-&
[5]   ELECTRODISSOLUTION OF COPPER-NICKEL ALLOYS [J].
BOCKRIS, JO ;
DESPIC, A ;
LOVRECEK, B ;
RUBIN, BT .
ELECTROCHIMICA ACTA, 1972, 17 (05) :973-&
[6]   KINETICS OF ANODIC DISSOLUTION OF COPPER IN ACID CHLORIDE SOLUTIONS [J].
BONFIGLIO, CH ;
ALBAYA, HC ;
COBO, OA .
CORROSION SCIENCE, 1973, 13 (10) :717-724
[7]  
CASTLE JE, 1985, 10 COPP DEV ASS PAP
[8]  
CHAUHAN PK, 1985, CORROS SCI, V25, P65
[9]   AN X-RAY PHOTO-ELECTRON SPECTROSCOPIC INVESTIGATION OF THE AIR-FORMED FILM ON COPPER [J].
CHAWLA, SK ;
RICKETT, BI ;
SANKARRAMAN, N ;
PAYER, JH .
CORROSION SCIENCE, 1992, 33 (10) :1617-1631
[10]   X-RAY PHOTOELECTRON-SPECTROSCOPY ANALYSIS OF COPPER AND ZINC-OXIDES AND SULFIDES [J].
DEROUBAIX, G ;
MARCUS, P .
SURFACE AND INTERFACE ANALYSIS, 1992, 18 (01) :39-46