PREFERRED ORIENTATION OF PITCH PRECURSOR FIBERS AND CARBON-FIBERS PREPARED FROM ISOTROPIC PITCH

被引:9
作者
HAMADA, T
FURUYAMA, M
TOMIOKA, T
ENDO, M
机构
[1] THREE D COMPOSITES RES CORP,TSUKUBA 305,JAPAN
[2] SHINSHU UNIV,FAC ENGN,MATSUMOTO,NAGANO 390,JAPAN
关键词
D O I
10.1557/JMR.1992.1178
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The preferred orientation of pitch precursor fibers and carbon fibers from an isotropic pitch was studied using x-ray diffraction techniques. The phi-scan profile of a pitch precursor fiber was divided into two parts: phi-scan-dependent (anisotropic) and phi-scan-independent (isotropic) profiles. The half width at half maximum (HWHM) intensity of the anisotropic part became smaller as the pitch viscosity increased during spinning and as the filament diameter decreased. The area ratio of the anisotropic part to the total area increased when spinning at higher pitch viscosities and when making the diameter thinner; no preferred orientation existed for pitch precursor fibers with very large diameters. A thermodynamic model is proposed for the preferred orientation formation when spinning an isotropic pitch. The carbon fiber exhibited no skin-core difference in preferred orientation. A crystallite with a larger crystallite size L(c)(002) in the carbon fiber was shown to be better aligned along the fiber axis than that with a smaller L(c)(002). Furthermore, a well-aligned crystallite possessed a larger L(c)(002) than one that was misaligned. The pitch precursor fiber also exhibited such a correlation between L(c)(002) and the preferred orientation, but the correlation was weak.
引用
收藏
页码:1178 / 1188
页数:11
相关论文
共 32 条
[21]   PREPARATION OF HIGHLY-ORIENTED CARBON FIBER FROM PITCH MATERIAL [J].
OTANI, S ;
KOKUBO, Y ;
KOITABASHI, T .
BULLETIN OF THE CHEMICAL SOCIETY OF JAPAN, 1970, 43 (10) :3291-+
[22]  
OTANI S, 1978, SEN GAKKAI SHI, V34, P250
[23]  
OTANI S, 1986, TANSO SEN, P173
[24]  
Ruland W., 1969, APPL POLYM S, V9, P293
[25]  
Shimizu J., 1977, SEN-I GAKKAISHI, V33, P208
[26]   EXPERIMENTAL TEST ON ESTIMATION OF AROMATIC LAYER SIZE DISTRIBUTION PROPOSED BY DIAMOND,R [J].
SHIRAISHI, M ;
KOBAYASH.K .
NIPPON KAGAKU KAISHI, 1972, (06) :1135-+
[27]   MESOPHASE AND HIGH MODULUS CARBON-FIBERS FROM PITCH [J].
SINGER, LS .
CARBON, 1978, 16 (06) :409-415
[28]   CARBON-FIBERS FROM MESOPHASE PITCH [J].
SINGER, LS .
FUEL, 1981, 60 (09) :839-847
[29]   SIZE EFFECTS IN ELECTRICAL-PROPERTIES OF BENZENE-DERIVED GRAPHITE FIBERS [J].
TAHAR, MZ ;
DRESSELHAUS, MS ;
ENDO, M .
CARBON, 1986, 24 (01) :67-72
[30]  
TILLGNER H, 1987, 18TH BIENN C CARB, P28