STRUCTURAL AND TEXTURAL CHANGES FROM POLYIMIDE KAPTON TO GRAPHITE .1. OPTICAL MICROSCOPY AND TRANSMISSION ELECTRON-MICROSCOPY

被引:50
作者
BOURGERETTE, C [1 ]
OBERLIN, A [1 ]
INAGAKI, M [1 ]
机构
[1] HOKKAIDO UNIV,FAC ENGN,DEPT APPL CHEM,SAPPORO,HOKKAIDO 060,JAPAN
关键词
D O I
10.1557/JMR.1992.1158
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Kapton films, 25-mu-m thick, were carbonized and then graphitized at various temperatures up to 3000-degrees-C. They were studied by optical microscopy and transmission electron microscopy and were prepared by thin-sectioning for transmission electron microscopy. The residual embedded blocks were used as polished sections for optical microscopy. Kapton thin film heat-treated at 650-degrees-C showed thin areas of preferred orientation at its two opposite faces. This orientation extends all over the film thickness between 800-degrees-C and 1000-degrees-C. It corresponds to a statistical orientation of small aromatic layer stacks, parallel to the film plane. From 1000-degrees-C up to 2475-degrees-C flattened pores develop everywhere. At 2475-degrees-C, they suddenly collapse and partial graphitization occurs. The Kapton film is completely graphitized between 2820-degrees-C and 3000-degrees-C. The mechanism of graphitization is similar to that of anthracites and also to that of nongraphitizing carbons heat-treated under pressure.
引用
收藏
页码:1158 / 1173
页数:16
相关论文
共 21 条
  • [1] BOULMIER JL, 1982, SCANNING ELECTRON MI, V4, P1523
  • [2] POLYIMIDES AS PRECURSORS FOR ARTIFICIAL CARBON
    BURGER, A
    FITZER, E
    HEYM, M
    TERWIESCH, B
    [J]. CARBON, 1975, 13 (03) : 149 - 157
  • [3] CHARACTERIZATION BY ELECTRON-MICROSCOPY OF CARBON PHASES (INTERMEDIATE TURBOSTRATIC PHASE AND GRAPHITE) IN HARD CARBONS WHEN HEAT-TREATED UNDER PRESSURE
    DEFONTON, S
    OBERLIN, A
    INAGAKI, M
    [J]. JOURNAL OF MATERIALS SCIENCE, 1980, 15 (04) : 909 - 917
  • [4] CRYSTALLITE GROWTH IN GRAPHITIZING AND NON-GRAPHITIZING CARBONS
    FRANKLIN, RE
    [J]. PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1951, 209 (1097): : 196 - &
  • [5] MICROTEXTURE AND STRUCTURE OF HIGH-TEMPERATURE MASSIVE PYROCARBONS PREPARED ON GRAPHITE SUBSTRATES
    GOMA, J
    OBERLIN, A
    [J]. CARBON, 1985, 23 (01) : 85 - 90
  • [6] STRUCTURE AND PROPERTIES OF HIGHLY CRYSTALLIZED GRAPHITE FILMS BASED ON POLYIMIDE KAPTON
    HISHIYAMA, Y
    YASUDA, S
    YOSHIDA, A
    INAGAKI, M
    [J]. JOURNAL OF MATERIALS SCIENCE, 1988, 23 (09) : 3272 - 3277
  • [7] HISHIYAMA Y, 1988, GRAPHITE INTERCALATI, P231
  • [8] MICROTEXTURE OF NONGRAPHITIZING CARBONS AND TEM STUDIES OF SOME ACTIVATED SAMPLES
    HUTTEPAIN, M
    OBERLIN, A
    [J]. CARBON, 1990, 28 (01) : 103 - 111
  • [9] Inagaki M., 1977, High Temperatures - High Pressures, V9, P453
  • [10] CARBONIZATION OF POLYIMIDE FILM KAPTON
    INAGAKI, M
    HARADA, S
    SATO, T
    NAKAJIMA, T
    HORINO, Y
    MORITA, K
    [J]. CARBON, 1989, 27 (02) : 253 - 257