DRAWING OF PD77.5CU6SI16.5 METALLIC GLASS WIRES

被引：46

作者：

TAKAYAMA, S

机构：

[1] Department of Metallurgy and Materials Science, University of Pennsylvania, Philadelphia

来源：

MATERIALS SCIENCE AND ENGINEERING | 1979年 / 38卷 / 01期

关键词：

D O I：

10.1016/0025-5416(79)90030-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Wires of Pd77.5Cu6Si16.5 metallic glass were cold drawn using diamond dies. A total area reduction of up to about 93% can be obtained after multiple passes through appropriate dies. After drawing two families of surface marking are observed: the traces of one set make an angle of about 41° to the wire axis while the other is nearly perpendicular to it. Tensile tests conducted on both drawn and undrawn wires show fracture on planes that always deviate from the 45° maximum shear plane. The fracture stresses of drawn wires are found to be slightly increased; the macroscopic elongation to break increases considerably after cold drawing. © 1979.

引用

页码：41 / 48

页数：8

共 24 条

[11] STRUCTURAL STABILITY AND MECHANICAL-PROPERTIES OF AMORPHOUS METALS [J].

MASUMOTO, T ;

MADDIN, R .

MATERIALS SCIENCE AND ENGINEERING, 1975, 19 (01) :1-24

[12] FATIGUE FRACTURE OF AMORPHOUS PD-20AT-PERCENTSI ALLOY [J].

OGURA, T ;

MASUMOTO, T ;

FUKUSHIMA, K .

SCRIPTA METALLURGICA, 1975, 9 (02) :109-113

[13] COMPREHENSIVE PLASTIC-DEFORMATION OF A BULK METALLIC GLASS [J].

PAMPILLO, CA ;

CHEN, HS .

MATERIALS SCIENCE AND ENGINEERING, 1974, 13 (02) :181-188

[14] STRENGTH AND FRACTURE CHARACTERISTICS OF FE, NI-FE AND NI-BASE GLASSES AT VARIOUS TEMPERATURES [J].

PAMPILLO, CA ;

POLK, DE .

ACTA METALLURGICA, 1974, 22 (06) :741-749

[15] FLOW OF MELT AND GLASS FORMS OF METALLIC ALLOYS [J].

POLK, DE ;

TURNBULL, D .

ACTA METALLURGICA, 1972, 20 (04) :493-&

[16] FRACTURE OF AMORPHOUS NI-PD-P ALLOYS [J].

TAKAYAMA, S ;

MADDIN, R .

PHILOSOPHICAL MAGAZINE, 1975, 32 (02) :457-470

[17] ROLLING AND BENDING DEFORMATION OF NI-PD-P METAL GLASSES [J].

TAKAYAMA, S ;

MADDIN, R .

ACTA METALLURGICA, 1975, 23 (08) :943-952

[18] TENSILE DEFORMATION OF AMORPHOUS NICKEL-PALLADIUM-PHOSPHOROUS ALLOYS [J].

TAKAYAMA, S ;

MADDIN, R .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (08) :1065-1072

[19] MECHANICAL-BEHAVIOR OF PARTIALLY CRYSTALLIZED AMORPHOUS ALLOYS [J].

TAKAYAMA, S ;

MADDIN, R .

JOURNAL OF MATERIALS SCIENCE, 1976, 11 (01) :22-26

[20] RESISTIVITY CHANGES BY DEFORMATION OF NI-PD-P AMORPHOUS ALLOYS [J].

TAKAYAMA, S ;

MADDIN, R .

SCRIPTA METALLURGICA, 1975, 9 (03) :343-347

← 1 2 3 →