ELECTROCHROMIC PROPERTIES OF SPIN-COATED THIN-FILMS FROM PEROXO-POLYMOLYBDOVANADATE SOLUTIONS

被引:12
作者
LI, YM
KUDO, T
机构
[1] Institute of Industrial Science, University of Tokyo, 7-22-1 Roppongi, Minato-ku
关键词
D O I
10.1149/1.2044151
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
A new mixed metal peroxo-polyacid based on Mo and V is formed by the direct reaction of a mixture of metallic Mo and V with hydrogen peroxide solution. A homogeneous amorphous thin film about 0.4 mu m is fabricated on an indium tin oxide (ITO) glass substrate by a spin-coating technique using this peroxo-polymolybdovanadate solution. After heat-treatment from 80 to 120 degrees C in air for 1 h, it shows reversible electrochromism in an organic LiClO4 electrolyte solution, and changes color from greenish yellow to grayish violet and violet, depending on the intercalation level of Li. Cyclic-voltammograms of the mixed Mo/V oxide film and those of the end members (MoO3 and V2O3) are quite different from one another, both in shape and peak-current potential, indicating that each film has distinctly different intercalation electrochemistry. The potential (E) vs. composition (x, Li content per mol Mo0.5V0.5O2.75) diagram of the present film recorded in the intercalation process agrees with that of the deintercalation process in the range 0 < x < 1.5. The E-x relationship is approximated by two straight lines with different slopes, with a kink at x = 0.5. This suggests that in this film there are two kinds of sites with different site energies. The changes in electrochromic properties with heat-treatment are also discussed in relation to the microstructure of the film.
引用
收藏
页码:1194 / 1199
页数:6
相关论文
共 19 条
  • [11] PRUSSIAN-BLUE-MODIFIED ELECTRODES - AN APPLICATION FOR A STABLE ELECTROCHROMIC DISPLAY DEVICE
    ITAYA, K
    SHIBAYAMA, K
    AKAHOSHI, H
    TOSHIMA, S
    [J]. JOURNAL OF APPLIED PHYSICS, 1982, 53 (01) : 804 - 805
  • [12] PEROXOPOLYTUNGSTIC ACIDS SYNTHESIZED BY DIRECT REACTION OF TUNGSTEN OR TUNGSTEN CARBIDE WITH HYDROGEN-PEROXIDE
    KUDO, T
    OKAMOTO, H
    MATSUMOTO, K
    SASAKI, Y
    [J]. INORGANICA CHIMICA ACTA, 1986, 111 (02) : L27 - L28
  • [13] KUDO T, 1990, 2ND P AS C SOL STAT, P191
  • [14] SATO S, 1982, IECE T C, V65, P829
  • [15] ELECTROCHROMIC THIN-FILMS COATED FROM PEROXO-POLYMOLYBDOTUNGSTATE SOLUTIONS
    TAKANO, S
    KISHIMOTO, A
    HINOKUMA, K
    KUDO, T
    [J]. SOLID STATE IONICS, 1994, 70 : 636 - 641
  • [16] THERMODYNAMIC AND MASS-TRANSPORT PROPERTIES OF LIAL
    WEN, CJ
    BOUKAMP, BA
    HUGGINS, RA
    WEPPNER, W
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1979, 126 (12) : 2258 - 2266
  • [17] PEROXOTUNGSTIC ACID COATED FILMS FOR ELECTROCHROMIC DISPLAY DEVICES
    YAMANAKA, K
    OAKAMOTO, H
    KIDOU, H
    KUDO, T
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1986, 25 (09): : 1420 - 1426
  • [18] ELECTROCHROMIC PROPERTIES OF V2O5 THIN-FILMS COLLOID-CHEMICALLY DEPOSITED ONTO ITO GLASSES
    YOSHINO, T
    BABA, N
    KOUDA, Y
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 1987, 26 (05): : 782 - 783
  • [19] SPECTROSCOPIC AND ELECTROCHEMICAL STUDIES OF ELECTROCHROMIC HYDRATED NICKEL-OXIDE FILMS
    YU, PC
    NAZRI, G
    LAMPERT, CM
    [J]. SOLAR ENERGY MATERIALS, 1987, 16 (1-3): : 1 - 17