SPALLING RESISTANCE OF CEMENTED CARBIDE WITH PHYSICALLY AND CHEMICALLY VAPOR-DEPOSITED COATINGS

被引:8
作者
RICH, DJ
PERRY, AJ
WOERNER, PF
机构
[1] GTE Valenite Corp, Troy, MI, USA, GTE Valenite Corp, Troy, MI, USA
关键词
MICROSCOPIC EXAMINATION - TITANIUM COMPOUNDS - Vapor Deposition;
D O I
10.1016/0040-6090(87)90383-X
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
As a previous study had indicated that cemented carbide inserts coated with TiN by physical vapor deposition (PVC) methods have lower spalling resistance than those coated by chemical vapor deposition (CVD), in the present work the mode of loss caused by the milling of nodular cast iron was studied. It is found that CVD coatings may begin to fail cohesively but failure always causes damage well into the substrate. In contrast, PVD coatings always begin to fail cohesively and the areas expand and reach down to the substrate; adhesive loss causes less substrate damage. Scratch tests performed at loads well above the critical load appear to show the same characteristics of crack propagation as found during the coating loss in the milling studies.
引用
收藏
页码:417 / 424
页数:8
相关论文
共 13 条
[1]  
BUHL R, 1981, THIN SOLID FILMS, V80, P245
[2]  
CHO T, 1985, ASM8512016 AM SOC ME
[3]   THE STRESS IN ION-PLATED HFN AND TIN COATINGS [J].
CHOLLET, L ;
PERRY, AJ .
THIN SOLID FILMS, 1985, 123 (03) :223-234
[4]  
MOLL E, 1980, Patent No. 4197175
[5]  
Perry A. J., 1986, Surface Engineering, V2, P183
[6]   VARIATIONS IN THE COLOR OF GROUP-IV B-NITRIDE FILMS [J].
PERRY, AJ ;
SCHOENES, J .
VACUUM, 1986, 36 (1-3) :149-155
[7]  
RICH DJ, 1986, J VAC SCI TECHNOL A, V4, P2757
[8]  
SASAKI K, 1982, REFRACT HARD MET, V1, P157
[9]   REACTIVELY SPUTTERED NITRIDES AND CARBIDES OF TITANIUM, ZIRCONIUM, AND HAFNIUM [J].
SPROUL, WD .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (06) :2874-2878
[10]  
STEINMANN PA, 1985, MATER TECHNOL, V13, P85