MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF ION-BEAM-PRODUCED FE-TI-(N), FE-TI-(C), AND FE-TI-(C,N) SURFACE-FILMS

Ion-mixed films of Fe53 Ti47 were produced by ion irradiating a Fe-Ti multilayer structure on AISI 304 stainless steel. The ion-mixed films were subsequently implanted with nitrogen, carbon, or both carbon and nitrogen. The microstructure following nitrogen implantation consisted of a bcc solid solution of iron and titanium and finely dispersed TiN precipitates. In the cases of carbon or carbon and nitrogen implantation, a two-phase structure consisting of an amorphous matrix with TiC or Ti(C,N) precipitates was found. All these films initially possessed improved tribological properties as revealed by lowered friction and increased wear resistance. However, after an extended test of 1000 wear cycles, a reduced friction was only observed for the carbon or carbon and nitrogen implanted samples. The wear track on the dual implanted surface was extremely smooth, while the surface of the nitrogen-implanted sample was partly worn through, causing the friction to increase to the level of the untreated sample. The improved tribological properties of the implanted films are attributed to an increase in surface hardness. However, the surface hardness is unable to explain differences between different implantations. In the case of the dual carbon and nitrogen implantation, improvements appear to be in part the result from an increased capability to accommodate plastic deformation. These conclusions are supported by transmission electron microscope studies of the wear tracks as well as by nanoindentation measurements.