HYDROGEN INDUCED FRACTURE OF A HIGH-STRENGTH ALUMINUM-ALLOY

被引：36

作者：

KOCH, GH

机构：

来源：

CORROSION | 1979年 / 35卷 / 02期

关键词：

D O I：

10.5006/0010-9312-35.2.73

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A fractographic study was carried out on intergranular and transgranular cracks produced in the commercial aluminum alloy 7075 in a 3% NaCl aqueous solution and in ionized hydrogen gas. It is demonstrated that fracture in both environments is similar, suggesting a common mechanism of crack growth. It is concluded that stress corrosion cracking (SCC) is mechanical and involves hydrogen generated by the aqueous solution.

引用

页码：73 / 78

页数：6

共 23 条

[11] OCCURRENCE OF TRANSGRANULAR CLEAVAGE-LIKE FRACTURE IN AN AL-ZN-MG ALLOY DURING TENSILE TESTING [J].

NELSON, JL ;

PUGH, EN .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (07) :1459-1460

[12]

NELSON JL, 1976, THESIS U ILLINOIS

[13]

PUGH EN, 1977, MECHANISMS ENV SENSI, P493

[14] PRE-EXPOSURE EMBRITTLEMENT AND STRESS-CORROSION FAILURE IN AL-ZN-MG ALLOYS [J].

SCAMANS, GM ;

ALANI, R ;

SWANN, PR .

CORROSION SCIENCE, 1976, 16 (07) :443-459

[15]

Scully J.C., 1971, THEORY STRESS CORROS, P127

[16]

SEDRIKS AJ, 1969, T ASM, V62, P238

[17]

Speidel M.O., 1972, ADV CORROS SCI TECH, V2, P115, DOI DOI 10.1007/978-1-4615-8255-7_3

[18]

Speidel M.O., 1974, HYDROGEN METALS, P249

[19]

THOMPSON AW, 1976, REV COATINGS CORROSI, V2, P3

[20] HYDROGEN TRANSPORT BY DISLOCATIONS [J].

TIEN, JK ;

THOMPSON, AW ;

BERNSTEIN, IM ;

RICHARDS, RJ .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (06) :821-829

← 1 2 3 →