STRUCTURAL INVESTIGATIONS ON POLYMER LATICES BY SMALL-ANGLE X-RAY-SCATTERING

被引:11
作者
BALLAUFF, M
机构
[1] Polymer-Institut, Universität T.H, Karlsruhe, 76128
关键词
D O I
10.1002/masy.19940870112
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
An overview is given on recent studies of latices by small-angle x-ray scattering (SAXS). It is demonstrated that SAXS-studies performed at different contrast (contrast variation) allows the full elucidation of the fine structure of the particles down to a size-scale of a few nanometers. Examples are given including studies on core-shell latices composed of polystyrene (PS) and poly(methyl methacrylate) (PMMA) as well as of carboxylated latices.
引用
收藏
页码:93 / 101
页数:9
相关论文
共 36 条
[11]   THE INTERNAL STRUCTURE OF LAYERED COLLOIDAL PARTICLES DETERMINED WITH SANS [J].
DUITS, MHG ;
MAY, RP ;
DEKRUIF, CG .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1990, 23 :366-373
[12]   NEUTRON-SCATTERING FROM INTERFACIALLY POLYMERIZED CORE-SHELL LATEXES [J].
FISHER, LW ;
MELPOLDER, SM ;
OREILLY, JM ;
RAMAKRISHNAN, V ;
WIGNALL, GD .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1988, 123 (01) :24-35
[13]   A STUDY BY SMALL-ANGLE NEUTRON-SCATTERING OF THE SWELLING OF POLYSTYRENE LATEX-PARTICLES BY MONOMER [J].
GOODWIN, JW ;
OTTEWILL, RH ;
HARRIS, NM ;
TABONY, J .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1980, 78 (01) :253-256
[14]   SMALL-ANGLE X-RAY-ANALYSIS OF LATEX-PARTICLES WITH CORE-SHELL MORPHOLOGY [J].
GRUNDER, R ;
URBAN, G ;
BALLAUFF, M .
COLLOID AND POLYMER SCIENCE, 1993, 271 (06) :563-572
[15]  
Guinier G., 1955, SMALL ANGLE SCATTERI
[16]   THEORY OF INTERFACE BETWEEN IMMISCIBLE POLYMERS [J].
HELFAND, E ;
TAGAMI, Y .
JOURNAL OF POLYMER SCIENCE PART B-POLYMER LETTERS, 1971, 9 (10) :741-&
[17]  
KIM YS, UNPUB J POLYM SCI PC
[18]   ELIMINATION OF INTRAPARTICULAR BASE SCATTERING IN X-RAY SMALL ANGLE SCATTERING ON COMPACT PARTICLES .3. VERIFICATION ON SOLUTIONS OF MYOGLOBIN [J].
KIRSTE, RG ;
STUHRMANN, HB .
ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-FRANKFURT, 1967, 56 (5-6) :338-+
[19]   ON THE STRUCTURE AND CONFORMATION OF POLYMER-CHAINS IN LATEX-PARTICLES .1. SMALL-ANGLE NEUTRON-SCATTERING CHARACTERIZATION OF POLYSTYRENE LATEXES OF SMALL DIAMETER [J].
LINNE, MA ;
KLEIN, A ;
SPERLING, LH ;
WIGNALL, GD .
JOURNAL OF MACROMOLECULAR SCIENCE-PHYSICS, 1988, B27 (2-3) :181-216
[20]   SMALL-ANGLE NEUTRON-SCATTERING STUDIES OF INHOMOGENEITIES IN LATEX-PARTICLES FROM EMULSION HOMOPOLYMERIZATIONS [J].
MILLS, MF ;
GILBERT, RG ;
NAPPER, DH ;
RENNIE, AR ;
OTTEWILL, RH .
MACROMOLECULES, 1993, 26 (14) :3553-3562